The modification before the stabilization process could tune the exothermic behavior and the structural evolution of PAN fibers during stabilization. In this study, we demonstrate that a rapid thermal pretreatment in nitrogen can effectively mitigate the exothermic behavior of PAN fibers, such as decreasing the initial temperature, broadening the exothermal peak, and decreasing the nominal heat release during heating the fibers in air. The color of fibers has shown gradual changes from white to light yellow, yellow and brown during thermal pretreatment in nitrogen with the increase of pretreating temperature and time. The differential scanning calorimetry (DSC), Fourier Transform Infrared Spectrometer (FTIR), X-ray diffraction (XRD), and Thermogravimetric Analysis (TG) characterization have been applied to analyze the thermal properties, chemical and physical structural difference between PAN, and thermally pretreated PAN fibers. The thermal pretreatment of PAN fibers in nitrogen could induce cyclization, dehydrogenation, and cross-linking reactions, in which the cyclization play an important role on improving the cyclization index of stabilized PAN fibers. Meanwhile, the pretreatment can result in noticeable changes of the aggregation structure of PAN fibers, as indicated by the increase of crystallinity and crystalline size. These structural modifications can benefit the main cyclization reaction during stabilization and enhance the carbon yield in resultant carbon fibers. The rapid thermal pretreatment in nitrogen could increase efficiency of modification on PAN fibers, and that could save much time and energy. It is beneficial to manufacture low-cost carbon fibers and to spread the applications of carbon fibers.

Hollow glass microspheres (HGMs) can be used as thermal insulation materials owing to its hollow structure which brings excellent thermal insulation property and low density. At present, most researches on thermal conductivity of HGMs are focused on polymer matrix/HGMs composite materials. However, thermal conductivity of HGMs at vacuum in room temperature has rarely been investigated. In this work, thermal conductivity of six types of HGMs (T17 (0.17g/cm³), T20 (0.20g/cm³), T22 (0.22g/cm³), T25 (0.25g/cm³), T32 (0.32g/cm³) and T40 (0.40g/cm³)) at vacuum in room temperature were calculated by heat transfer of solid conduction and radiation. The calculation results showed that thermal conductivity of HGMs would be decreased by an order of magnitude compared with no vacuum. In order to verify the calculation and study vacuum thermal insulation properties of HGMs, thermal conductivity of above-mentioned HGMs at no vacuum and high vacuum in room temperature were measured by a self-made thermal conductivity measuring apparatus which was based on the transient plane source (TPS) method. The experimental results showed that thermal conductivity of HGMs were in the range of 4.2030E-02 to 6.3300E-02 W/m·K (at no vacuum) and 3.8160E-03 to 4.9660E-03 W/m·K (at high vacuum). The results indicated that experimental thermal conductivity was consistent with the calculation results and both of them were all decreased by 8-13 times at vacuum compared with no vacuum. In addition, the relationship with physical properties and thermal conductivity of HGMs has been discussed in detail. In conclusion, HGMs possess excellent thermal insulation performance at high vacuum in room temperature and have potential to further reduce thermal conductivity at the same conditions.