In this study, a novel organic/inorganic hybrid material containing cadmium sulfide (CdS) nanoparticles was synthesized in situ by using an all π-conjugated block copolymer as both a synergistic long-range ordered structure-directing template and an efficient exciton quencher for the nanohybrid. The conducting–conducting block copolymer of poly(2,5-dihexyloxy-para-phenylene)-b-poly(3-hexyl thiophene) (PPP-P3HT) was used as a linear nanoreactor for the quantum dot synthesis to yield nanohybrids with highly ordered donor/acceptor (D/A) nanowire morphology that exhibit enhanced optoelectronic properties. The synthesized PPP-P3HT/CdS-OH nanohybrid possessed a one-dimensional D/A coaxial nanowire structure of uniform width (∼10 nm), wherein the synthesized CdS quantum dots were embedded, resulting in a display of superior long-term stability in a solution medium. By a simple drop casting process, the hybrid materials with highly ordered organic/inorganic nanochannel arrays could also be preserved in a thin film state, as evidenced by TEM and X-ray measurements, for device applications. The PPP-P3HT block copolymer exhibited significantly better hole mobility than its P3HT homopolymer counterpart. In addition, the resulting PPP-P3HT/CdS-OH hybrid systems displayed a considerably enhanced PL quench effect and shorter exciton lifetime due to efficient charge transfer between the P3HT block and the confining CdS nanoparticles in the P3HT/CdS coaxial domain of the hybrid nanowire structure. Therefore, the PPP-P3HT/CdS-OH nanohybrids can be used as bicontinuous nanochannels for efficient charge separation and charge transport, which show potential for use in future optoelectronic applications.

In this study, nanopiezoelectric devices based on ZnO nanorod array/conducting polymers are fabricated for wearable power generation application. To replace the inorganic rigid indium-tin oxide (ITO) conducting coating commonly used in the nanogenerator devices, a series of flexible polyaniline-based conducting copolymers underlying the perpendicularly-oriented ZnO nanorod arrays has been synthesized with improved electric conductivity by the copolymerization of aniline and 3,4-ethylenedioxythiophene (EDOT) monomers in order to optimize the piezoelectric current collection efficiency of the devices. It is found that significantly higher conductivity can be obtained by small addition of EDOT monomer into aniline monomer solution using an in-situ oxidative polymerization method for the synthesis of the copolymer coatings. The highest conductivity of aniline-rich copolymer is 65 S/cm, which is 2.5 times higher than that for homopolymer polyaniline coating. Subsequently, perpendicularly-oriented ZnO nanorod arrays are fabricated on the polyaniline-based copolymer substrates via a ZnO nanoparticle seeded hydrothermal fabrication process. The surface morphology, crystallinity, orientation, and crystal size of the synthesized ZnO nanorod arrays are fully examined with various synthesis parameters for copolymer coatings with different monomer compositions. It is found that piezoelectric current generated from the devices is at least five times better for the device with improved electric conductivity of the copolymer and the dense formation of ZnO nanorod arrays on the coating. Therefore, these results demonstrate the advantage of using flexible π-conjugated copolymer films with enhanced conductivity to further improve piezoelectric performance for future wearable energy harvesting application based on all wet chemical coating processes.

An amphiphilic, Janus diblock hyperbranched copolyamide was synthesized by the condensation reaction, and the morphologies of aggregates in water were changed from spherical to dendritic-like structures via cylindrical-like structures in response to increasing temperature.