The conducting polymer of poly(3,4 ethylenedioxythiophene):poly(4-styrenesulfonate) (PEDOT:PSS) is one of the most important and intensively investigated organic conducting materials. The PEDOT:PSS water dispersions with various concentrations of poly (4-styrenesulfonic acid) solution (PSSAS) were synthesized by 3,4-ethylenedioxythiophene (EDOT) in the presence of water. The fabrication of the solvent-treated PEDOT:PSS films through spin coating and solvent treatment processes was achieved with a solvent of pure water mixed with acetone (or MeOH, EtOH) in a ratio of 50:50. Moreover, both the organic solvent and water have synergetic effects while the PSS and PEDOT-attached PSS segments will form a coil-like and a linear (or extended-coil) structure, respectively. That may induce a stacking of the linear and planar PEDOT-attached PSS segments, which favors the formation of a crystalline phase. Finally, the maximum electrical conductivity of the PEDOT:PSS thin films with solvent treatment was investigated by means of X-ray diffraction (XRD) patterns and scanning electron microscope (SEM) images. Furthermore, we aimed to explain the synergetic effects of phase separation of the PEDOT:PSS thin films by both the organic solvent and water.

N¹, N⁶-bis (4-aminobutyl) adipamide (BABA) diamine and sebacic acid (SA), also called BABA/SA polyamide salt, were used in a typical melt polymerization processes of polyamide 6 (PA6) to form a series of PA6-BABA/SA copolyamides. The effects of BABA/SA on the isothermal crystallization kinetics of PA6-BABA/SA were studied for the first time. An isothermal crystallization analysis demonstrates that the PA6-BABA/SA matrix provided a higher crystallization rate and shorter half-crystallization time than virgin PA6 did. The degree of crystallization of the PA6-BABA/SA₃₀ matrix was also the lowest among all of the samples considered herein. This result is attributed to the high nucleation efficacy of a small amount of BABA/SA in the crystallization of PA6. Values of the Avrami exponent (n) from 1.84 to 3.91 were observed for all of the polyamide samples, suggesting that the crystallization was involved via a two- to three-dimensional growth mechanism. These findings deepen our understanding of the structure–property relationship of PA6-BABA/SA copolyamides, favoring their practical application.

This work investigated the synthesis of a novel low melting temperature polyamide 6 (PA6) copolyamide (PA6-BABT/SA) with different aliphatic/aromatic units weight content using a melt poly-condensation process. The bio-based aromatic N¹,N⁴-bis(4-aminobutyl) terephthalamide diamine (BABT) and long-chain aromatic polyamide salt (BABT/SA, salt of BABT, and sebacic acid), components used for the synthesis of copolyamides, were obtained from bio-based monomers. For the first time, the pertinent BABT/SA aromatic polyamide salt was isolated as a white solid and completely characterized. By varying the weight ratio of BABT/SA salt, a series of copolyamides with different molecular weights and physical properties were prepared. The aromatic BABT/SA salt disrupted crystallization of the final copolyamides and lowered the onset of melting. The Fourier transform infrared spectroscopy and X-ray diffraction results indicated a steady decrease in the degrees of crystallinity with increasing BABT/SA salt segment ratio. Furthermore, compared to neat PA6, the obtained PA6-BABT/SA copolymers possessed a similar thermal stability and high transparency, but lower glass transition temperature around human body temperature. The PA6-BABT/SA copolymers with number-average molecular weight ≥30,000 Da presented good mechanical properties, specifically showing excellent tensile strength and elongation at break up to 105.2 MPa and 218.3%, respectively.