Novel bionanocomposite films of chitosan/montmorillonite (CS/MMT) activated with ginger essential oil (GEO) were produced and characterized in terms of their physical and morphological properties. The homogenization process led to a good interaction between the chitosan and the nanoparticles, however the exfoliation was diminished when GEO was incorporated. Film glass transition temperature did not statistically change with the incorporation of either MMT or GEO, however the value was slightly reduced, representing a relaxation in the polymer chain which corroborated with the mechanical and barrier properties results. Pristine chitosan films showed excellent barrier properties to oxygen with a permeability of 0.184 × 10⁻¹⁶ mol/m·s·Pa being reduced to half (0.098 × 10⁻¹⁶ mol/m·s·Pa) when MMT was incorporated. Although the incorporation of GEO increased the permeability values to 0.325 × 10⁻¹⁶ mol/m·s·Pa when 2% of GEO was integrated, this increment was smaller with both MMT and GEO (0.285 × 10⁻¹⁶ mol/m·s·Pa). Bionanocomposites also increased the UV light barrier. Thus, the produced bioplastics demonstrated their ability to retard oxidative processes due to their good barrier properties, corroborating previous results that have shown their potential in the preservation of foods with high unsaturated fat content.

The aim of this work was to develop an active biopolymer based on chitosan by incorporating natural antioxidants. Five essential oils (ginger, rosemary, sage, tea tree and thyme) and six hydro-alcoholic extracts (from ginger, green and black tea, kenaf leaves, rosemary and sage plants) were tested. Migration assays were carried out to evaluate the films’ activity, and total phenolic content and antioxidant activity were monitored in the simulant during storage. Interaction between natural compounds and polymeric matrix was evaluated by FTIR spectroscopy. The diffusion of the phenolic compounds was not detected in the films incorporated with hydro-alcoholic extracts (HAEs), indicating their entrapment in the chitosan. Migration was observed in the films with essential oils (EOs), and biobased films incorporated with ginger, sage or rosemary essential oils, presented the highest diffusion and antioxidant activity in the simulant, highlighting their functionality and potential to be used as food active packaging material.