In this study, coating equipment for the effective underwater repair of submerged structures was developed. The tensile bond characteristics of selected epoxy resin coatings were investigated by coating the surface of a specimen using each of the four types of equipment. Using the experimental results, the tensile bond strength and the coating thickness were analyzed according to the type of equipment, coating, and curing time. The results show that the type of coating equipment used had the greatest effect on the measured bond strength and coating thickness of the selected coatings. However, the effect of coating type and curing time on the bond strength and the thickness was observed to be insignificant. Compared with the developed equipment, the surface treatment of the coating was observed to be more effective when using the pre-existing equipment, and thus the bond performance of the coating was improved compared to using the pre-existing equipment. Based on the experimental results, improvements and needs involving the equipment for further research were discussed.

This study investigated changes in the interfacial properties of epoxy-coated concrete exposed to various conditions, regarding the epoxy type, coating equipment, and exposure environment and period. The measured coating thickness and pull-off bond strength exhibited diverse trends, depending on the exposure period and conditions. In the real sea (RS) environment, the average bond strengths for bisphenol A (BPA) (E1), BPA with zinc powder (E2), and BPA with cresyl glycidyl ether (E3) were 1.26, 1.93, and 1.92 MPa, respectively. The coating method did not significantly affect the measured coating thickness and strength values. The conventional roller (D1) exhibited the highest thickness variation, with a value of 214.45 μm. The RS condition significantly increased the coating thickness (34% to 158%) compared to the tap water (TW) condition. The exposure conditions had little impact on bond strength except for E3, which showed an increased strength (2.71 MPa) over 7–91 days, especially under RS conditions, while E2 remained constant at approximately 1.82 MPa. This study offers insights into factors influencing marine concrete coating performance and discusses limitations and future work.

This study aims to investigate the effects of different exposure conditions on the interfacial bond between steel plates and epoxy resin coatings at early ages. Test variables include the epoxy resin types, exposure conditions, exposure periods, and coating equipment. The selected epoxy resins were applied to prepared steel plates and cured at each exposure condition for 7, 28, 56, or 91 days, and the pull-off bond strength and coating thickness were measured. Scanning electron microscopy (SEM) images were obtained to study the interfacial bond for some representative coatings. Three different exposure conditions (indoors and actual marine environment) were considered in this study. This study is also focusing on the improvement of previously developed underwater coating equipment and evaluating the performance. Experiments were conducted to evaluate the performance of the improved equipment types under different environmental conditions: indoors (tap water and seawater) and outdoor conditions. The improved equipment types were confirmed to be effective for underwater coating and easier to use than the previous equipment under real sea conditions. The experimental results also confirmed that the bond strength of the coating decreased as the curing time increased.

In this study, a modular FRP DSCT(Modular Fiber-Reinforced Polymer Double-Skinned Composite Tubular) column was suggested, and bending performance was experimentally evaluated. Two specimens were designed, a monotype and a modular type, and quasi-static tests were conducted to investigate the bending strength of the modular type in order to compare its strength with the monotype. To calculate the number of bolts needed and the bolt diameter for the modular type, the maximum stress result acting on the FRP tube from nonlinear analysis was applied. The test was carried out by increasing the drift ratio, and as a result of the test, the moment, lateral load, displacement, and dissipation energy were calculated. The test results showed that there was no significant difference in maximum displacement between the monotype and the modular type, but the modular type showed a strength approximately 30% lower than that of the monotype. For the displacement ductility and the energy ductility, it resulted in values 1.4% and 3.5% higher than those of the monotype, respectively. Therefore, it is necessary to develop an enhanced connector or to consider a reduction factor in designing a modular DSCT column.

To enhance effectiveness and efficiency of wind power generation, size of wind turbine and the height of the tower have been enlarged. Recently, many researches to develop generating systems combined with wind energy and other renewable energies are being conducted. In this study, section design of tower structure supporting a wind turbine and two tidal turbines was suggested by applying a DSCT structure. An automatic design tool for DSCT columns, AutoDSCT program was used to generate new bottom sections of the tower with different hollow ratios and thicknesses of each tube. The DSCT towers with suggested design sections were carried out with moment resisting performance evaluation through nonlinear analysis in CoWiTA program.