Plastic waste is an issue of global concern because of the environmental impact of its accumulation in waste management systems and ecosystems. Biodegradability was proposed as a solution to overcome this problem; however, most biodegradable plastics were designed to degrade under aerobic conditions, ideally fulfilled in a composting plant. These new plastics could arrive to anaerobic environments, purposely or frequently, because of their mismanagement at the end of their useful life. This review analyzes the behavior of biodegradable and conventional plastics under anaerobic conditions, specifically in anaerobic digestion systems and landfills. A review was performed in order to identify: (a) the environmental conditions found in anaerobic digestion processes and landfills, as well as the mechanisms for degradation in those environments; (b) the experimental methods used for the assessment of biodegradation in anaerobic conditions; and (c) the extent of the biodegradation process for different plastics. Results show a remarkable variability of the biodegradation rate depending on the type of plastic and experimental conditions, with clearly better performance in anaerobic digestion systems, where temperature, water content, and inoculum are strictly controlled. The majority of the studied plastics showed that thermophilic conditions increase degradation. It should not be assumed that plastics designed to be degraded aerobically will biodegrade under anaerobic conditions, and an exact match must be done between the specific plastics and the end of life options that they will face.

Different degradable plastics have been promoted as a solution for the accumulation of waste in landfills and the natural environment; in Mexico, the most popular options are oxo-degradable, which degrade in a sequential abiotic–biotic process, and compostable plastics. In this research, high-density polyethylene, oxo-degradable high-density polyethylene, and certified compostable plastic were exposed to simulated landfill conditions in an 854-day-long experiment to assess their degradation. High-density polyethylene showed limited degradation, due mainly to surface erosion, evidenced by a 13% decrease in elongation at break. The pro-oxidant additive in the oxo-degradable plastic increased this loss of mechanical properties to 27%. However, both plastic films kept their physical integrity and high molecular weight by the end of the experiment, evidencing degradation but no biodegradation. While the compostable film fragmented, had a lower molecular weight at the end of the experiment, and decreased the presence of C=O bonds, this degradation took place remarkably slower than expected from a composting process. Results show that oxo-degradable and compostable plastics will not biodegrade readily in landfills. This fact should be known and understood for decision-makers to match the characteristics of the materials to the features of the waste management systems.