The development of non-cellularized composites of chitosan (CHI) hydrogels, filled with cellulose nanofibers (CNFs) of the type nanofibrillated cellulose, was proposed for the repair and regeneration of the intervertebral disc (IVD) annulus fibrosus (AF) tissue. With the achievement of CNF-filled CHI hydrogels, biomaterial-based implants were designed to restore damaged/degenerated discs. The structural, mechanical and biological properties of the developed hydrogel composites were investigated. The neutralization of weakly acidic aqueous CNF/CHI viscous suspensions in NaOH yielded composites of physical hydrogels in which the cellulose nanofibers reinforced the CHI matrix, as investigated by means of microtensile testing under controlled humidity. We assessed the suitability of the achieved biomaterials for intervertebral disc tissue engineering in ex vivo experiments using spine pig models. Cellulose nanofiber-filled chitosan hydrogels can be used as implants in AF tissue defects to restore IVD biomechanics and constitute contention patches against disc nucleus protrusion while serving as support for IVD regeneration.

We have developed a new experimental methodology to investigate the adhesive properties of hydrogels on solid surfaces under fully immersed conditions. The method, based on contact mechanics, provides time-resolved reproducible and quantitative data on the work of adhesion between a hydrogel at swelling equilibrium and a planar surface grafted with responsive brushes. We used poly(N,N-dimethylacrylamide) (PDMA) and polyacrylamide (PAM) as model gels and poly(acrylic acid) (PAA) as pH dependent polymer brush. The effect of pH, contact time and debonding velocity on adhesive interactions was specifically investigated. As expected from molecular interactions, we found that adhesion increased as the pH decreased and this was attributed to the formation of hydrogen bonds at the interface. Surprisingly, however, the buildup of adhesion increased slowly with the time of contact up to one hour and depended markedly on debonding velocity despite the very elastic nature of the hydrogels. Furthermore, the maximum pH where adhesion was observed was significantly higher for the couple PAM–PAA than for the couple PDMA–PAA, in contrast with the onset of molecular interactions in dilute solutions.

Soft tissues are commonly fiber-reinforced hydrogel composite structures, distinguishable from hard tissues by their low mineral and high water content. In this work, we proposed the development of 3D printed hydrogel constructs of the biopolymers chitosan (CHI) and cellulose nanofibers (CNFs), both without any chemical modification, which processing did not incorporate any chemical crosslinking. The unique mechanical properties of native cellulose nanofibers offer new strategies for the design of environmentally friendly high mechanical performance composites. In the here proposed 3D printed bioinspired CNF-filled CHI hydrogel biomaterials, the chitosan serves as a biocompatible matrix promoting cell growth with balanced hydrophilic properties, while the CNFs provide mechanical reinforcement to the CHI-based hydrogel. By means of extrusion-based printing (EBB), the design and development of 3D functional hydrogel scaffolds was achieved by using low concentrations of chitosan (2.0–3.0% (w/v)) and cellulose nanofibers (0.2–0.4% (w/v)). CHI/CNF printed hydrogels with good mechanical performance (Young’s modulus 3.0 MPa, stress at break 1.5 MPa, and strain at break 75%), anisotropic microstructure and suitable biological response, were achieved. The CHI/CNF composition and processing parameters were optimized in terms of 3D printability, resolution, and quality of the constructs (microstructure and mechanical properties), resulting in good cell viability. This work allows expanding the library of the so far used biopolymer compositions for 3D printing of mechanically performant hydrogel constructs, purely based in the natural polymers chitosan and cellulose, offering new perspectives in the engineering of mechanically demanding hydrogel tissues like intervertebral disc (IVD), cartilage, meniscus, among others.

The controlled complex coacervation of oppositely charged hyaluronic acid (M_w ≈ 800–1000 kg mol⁻¹) and chitosan (M_w ≈ 160 kg mol⁻¹, degree of acetylation = 15%) led to hydrogels with controllable properties in terms of elasticity and strength. In this work, we performed desalting by dialysis of high ionic strength solutions of mixed polyelectrolytes and showed that the control of the pH during the polyelectrolyte assembly greatly impacts the mechanical properties of the hydrogel. First, for pHs from 5.5 to 7.5, a slight coacervation was observed due to low chitosan protonation and poor polyelectrolyte associations. Then, for pHs from 3.0 to 5.5, coacervation and syneresis led to free-standing and easy to handle hydrogels. Finally, for pHs from 2.0 to 3.0 (close to the pK_a of the hyaluronic acid), we observed the unusual stretchability of these hydrogels that could arise from the pre-folding of hyaluronic acid chains while physical crosslinking was achieved by hyaluronic acid/chitosan polyelectrolyte complexation.