Ultrasound-assisted transient liquid phase bonding (U-TLP) has been regarded as a promising brazing process to join magnesium alloys with a Sn and Zn interlayer; however, the formation of brittle magnesium intermetallic compounds (Mg₂Sn, MgZn, and MgZn₂) compromises the mechanical properties of the joints. In this study, Mg alloy U-TLP joints with a Ni interlayer were evaluated based on shear strength and hardness measurement. Microstructural evolution along with ultrasonic duration time and intermetallic compound formation were characterized using X-ray diffraction and electron microscopy methods. The results show that incremental ultrasonic durations of up to 30 s lead to the microstructural evolution from the Mg₂Ni layer, eutectic compounds (Mg₂Ni and α-Mg) to α-Mg (Ni), accompanied by shear strength increases. The maximum value of the shear strength is 107 MPa. The role that ultrasound vibration played in brazing was evaluated, and showed that the MgO film was broken by the acoustic softening effect when the interlayer and base metal were solid. As the MgO and Mg substrate have different stress reduction τ, this plastic mismatch helps to break the oxide film. Additionally, the diffusion between the solid Mg substrate and Ni interlayer is accelerated greatly by the acoustic pressure based on the DICTRA dynamic calculation.

An additive manufacturing (AM) method for the deposition of metallic layer in micron scale on monocrystalline silicon wafer surface by high voltage induced weak electric arc machining (HV-μEAM) has been proposed. The process characteristics of HV-μEAM are analyzed to fulfil the metal material deposition. The influence of the processing parameters on the deposition effect were studied with copper as additive electrode material. Using the optimal parameters, a number of complex trajectory deposition experiments have been carried out and a QD character-type deposition layer with a height of 139.09 μm has been obtained. The deposition has good continuity and high forming precision. It is proven that the new method is achievable and efficient for patterning metallic materials in the micro- and nano-scale on the silicon substrates surface.

Titanium alloys with special macro-micro composite structures of directional hydrophobicity are difficult to prepare due to poor thermal conductivity and good corrosion resistance, inhibiting the wide engineering applications for aerospace, marine engineering, and biomedicine. To prepare macro-micro composite structures on the surface of titanium alloys and achieve directional hydrophobicity, the sub-millimeter structures with an edge width of 150 μm, a groove width of 250 μm, and a depth of 250 μm were fabricated on the titanium alloy by wire electrical discharge machining (WEDM) technology, and high voltage-induced weak electric arc machining (HV-μEAM) was used to fabricate micro-scale feature size micro-structures on the processed macro-structure edges. The influence of process parameters on the morphology of microstructures was studied experimentally. The smooth surface of the titanium alloy is isotropically hydrophilic, and its contact angle is 68°. After processing the macrostructure on the titanium alloy surface, it shows directional hydrophobicity after being modified by low surface energy materials. The macro-micro composite structure formed by HV-μEAM realizes a directional hydrophobic surface with contact angles (CA) of 140° (parallel direction) and 130° (perpendicular direction), respectively. This surface has been modified with low surface energy to achieve contact angles of 154° and 143°. The results of the abrasion resistance test show that under the load of 100 g, it retains directional hydrophobicity at a friction distance of 700 mm with 600# sandpaper. The existence of the sub-millimeter macrostructure is the reason for the directionality of surface hydrophobicity. The microstructure can realize the transformation of the titanium alloy surface from hydrophilic to hydrophobic. Under the combined effects of the macro and micro composite structure, the surface of the titanium alloy shows obvious directional hydrophobicity.