This paper examines the influence of biochar on the properties of alkali-activated slag pastes using two activator solutions, namely NaOH and Na₂CO₃. The biochar demonstrated different absorption kinetics in the mixture of slag and the two activator solutions. The pastes with biochar showed a delay in the heat flow peak, compared to the pastes without biochar, but the cumulative heat release in these pastes at later hours was increased, compared to the pastes without biochar. It was found that the use of biochar reduced autogenous shrinkage in the pastes and the reduction in autogenous shrinkage was more pronounced in the alkali-activated slag with NaOH, compared to Na₂CO₃. The void structure of the pastes was investigated using x-ray micro-computed tomography. It was found that refined pore structure due to reduced effective solution/slag in the pastes with biochar was able to compensate for the decreasing effect of biochar voids on compressive strength. The electrical resistivity was shown to be lower in the pastes with biochar.

The effect of hydrogels containing nanosilica (NSi) on the autogenous shrinkage, mechanical strength, and electrical resistivity of cement pastes was studied. The interaction between the hydrogels and the surrounding cementitious matrix was examined using thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM). The addition of hydrogels decreased autogenous shrinkage in the cement pastes and this reduction showed a dependence on the concentration of NSi in the hydrogels. Compressive strength and electrical resistivity were reduced in the cement pastes with hydrogels and this reduction was decreased with increased concentration of NSi in the hydrogel. A change in the phase composition of the cement paste in the region close to the hydrogel was noted, compared to the region away from the hydrogel. In a lime solution with increased pH and temperature, Ca(OH)₂ and CaCO₃ were found to form within the hydrogels; evidence of calcium-silicate-hydrate (C-S-H) formation in the hydrogels with NSi was obtained, indicating the possible pozzolanic potential of the hydrogels with NSi.

The absorption and desorption of superabsorbent polymers (SAPs) in cement mixtures containing two different glass powders as supplementary cementitious materials are examined in this paper. Two SAPs with different chemical compositions were synthesized in-house and used in the experiments. SAP absorption was investigated directly through the mass change of SAPs in cement slurries, as well as indirectly using the flow test. Scanning electron microscopy was used to monitor the desorption of SAPs using samples prepared with freeze-drying. Hydration and setting time were evaluated to explain the desorption behavior of SAPs. SAP absorption generally increased in pastes with glass powders. The desorption rate of SAPs in different pastes was shown to correlate with the onset of solid skeleton development in the pastes. The addition of SAPs reduced autogenous shrinkage in neat cement paste more than in pastes with glass powders.