Studies on bonding of aluminium alloys to steels are popular because these are structural materials widely used in a variety of industries. However, joining these dissimilar materials is difficult mainly because of the formation of brittle intermetallic compounds. This paper presents a study on welding aluminium to steel by resistance spot welding. Before the welding, steel surface was covered by cold spraying with the layer of aluminium, nickel and nickel–aluminium. This way, instead of the welding of dissimilar materials, the welding of aluminium to aluminium (or nickel) layer pre-deposited on the steel sample was performed. The feasibility of using interlayers for improving the welding of dissimilar materials was tested using SEM, EDX and XRD. Mechanical properties of welds were investigated by microhardness and shear strength tests. The results showed that the coating allowed to decrease hardness in the welding zone and to increase the shear strength of the weld.

Nanocrystalline TiO₂ coatings were successfully deposited on metallic substrate surfaces through low-pressure cold spray. Sol–gel amorphous TiO₂ dry gel was for the first time used as a feedstock powder. Agglomerated morphology of the amorphous powder with high-density packing of particles and reduced pores number was an important factor for successful low-pressure cold spraying. However, in the present study one more factor contributing to anchoring of TiO₂ particles by cold gas spraying onto a substrate was indicated. This factor enabling effective powder deposition and coating production is based on an exotic for conventional ceramic materials’ plastic deformation of amorphous powder. Furthermore, the detailed analysis of SEM, Raman and XRD measurements clearly demonstrated that amorphous titanium dioxide is transformed into crystalline anatase form during the process of low-pressure cold spraying.