Lignin nanomaterials have wide application prospects in the fields of cosmetics delivery, energy storage, and environmental governance. In this study, we developed a simple and sustainable synthesis approach to produce uniform lignin nanoparticles (LNPs) by dissolving industrial lignin in deep eutectic solvents (DESs) followed by a self-assembling process. LNPs with high yield could be obtained through nanoprecipitation. The LNPs were characterized by dynamic light scattering (DLS), transmission electron microscopy (TEM), scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), and gel permeation chromatography (GPC). Distinct LNPs could be produced by changing the type of DES, lignin sources, pre-dropping lignin concentration, and the pH of the system. Their diameter is in the range of 20–200 nm and they show excellent dispersibility and superior long-term stability. The method of preparing LNPs from lignin–DES with water as an anti-solvent is simple, rapid, and environmentally friendly. The outcome aids to further the advancement of lignin-based nanotechnology.

A novel and effective green system consisting of deep eutectic solvent (DES) was proposed to prepare lignin nanoparticles (LNPs) without any lignin modification. The LNPs are obtained through the dialysis of the kraft lignin-DES solution. The particle size distribution, Zeta potential and morphology of the LNPs are characterized by using dynamic light scattering (DLS), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The average diameter of LNPs is in the range 123.6 to 140.7 nm, and the LNPs show good stability and dispersibility in water. The composite beads composed of LNPs and sodium alginate (SA) are highly efficient (97.1%) at removing methylene blue (MB) from the aqueous solution compared to 82.9% and 77.4% by the SA/bulk kraft lignin composite and pure SA, respectively. Overall, the LNPs-SA bio-nanocomposite with high adsorption capacity (258.5 mg/g) could be useful in improving water quality and other related applications.

Xylose residue (XR), after diluted acid treatment of corncob, consists of cellulose and lignin. However, structural changes of XR lignin have not been investigated comprehensively, and this has seriously hindered the efficient utilization of lignin. In this study, corncob milled wood lignin (CC MWL), and xylose residue milled wood lignin (XR MWL) were isolated according to the modified milled wood lignin (MWL) method. The structural features of two lignin fractions were thoroughly investigated via fourier transform infrared spectroscopy (FTIR), gel permeation chromatography (GPC), thermogravimetric analysis (TGA) and two dimensional nuclear magnetic resonance (2D NMR) spectroscopy techniques. XR MWL with higher yield and lower bound carbohydrate contents presented more phenolic OH contents than CC MWL due to partial cleavage of β-O-4. Furthermore, the molecular weights of XR MWL were increased, possibly because of condensation of the lignin during the xylose production. A study on antioxidant activity showed that XR lignin had better radical scavenging ability than that of 2,6-Di-tert-butyl-4-methyl-phenol (BHT) and CC MWL. The results suggested that the lignin in xylose residue, showing great antioxidant properties, has potential applications in food additives.