Potentiostatic electrodeposition was used to obtain CoCrFeMnNi high-entropy alloy (HEA) thin films on copper substrate. An electrolyte based on a DMSO (dimethyl sulfoxide)-CH₃CN (acetonitrile) organic compound was used for the HEA deposition. The microstructure of the high-entropy deposits before and after corrosion in artificial seawater was investigated by scanning electron microscopy (SEM) and energy dispersive spectrometry (EDS) investigation. SEM analysis revealed that compact and uniform film consists of compact and uniform 50 nm–5 μm particles that form the HEA films. The successful co-deposition of all five elements was highlighted by the energy dispersive spectrometry investigation (EDS). Electrochemical measurements carried out in an aerated artificial seawater solution under ambient conditions demonstrated the promising potential for application in the field of anti-corrosion protection, due to the protective behavior of the HEA thin films.

The paper is proposing a mini-review on the capability of the new complex concentrated alloys (CCAs) to substitute or reduce the use of critical raw materials in applications for extreme conditions. Aspects regarding the regulations and expectations formulated by the European Union in the most recent reports on the critical raw materials were presented concisely. A general evaluation was performed on the CCAs concept and the research directions. The advantages of using critical metals for particular applications were presented to acknowledge the difficulty in the substitution of such elements with other materials. In order to establish the level of involvement of CCAs in the reduction of critical metal in extreme environment applications, a presentation was made of the previous achievements in the field and the potential for the reduction of critical metal content through the use of multi-component compositions.

High-Entropy Alloys (HEAs) represent a transformative class of materials characterized by multiple principal elements and high configurational entropy. This review article provides an in-depth examination of their structural particularities, prediction methodologies, and synthesis techniques. HEAs exhibit unique structural stability due to high-entropy effects, severe lattice distortions, and slow diffusion processes. Predictive models, including thermodynamic and kinetic approaches, are essential for understanding phase stability. Various synthesis methods impact HEA properties, and advanced characterization techniques are crucial for their study. The article highlights current applications and future research directions, emphasizing the potential of HEAs in diverse technological fields.

In this paper, we investigate what effects heat treatment can have on potentiodynamically electrodeposited high-entropy thin film (HEA) CoCrFeMnNi alloys. We focused our study on the corrosion resistance in synthetic seawater, corroborated with the structure and microstructure of these thin films. Thin films of HEA alloys were deposited on a copper foil substrate, using an electrolyte based on the organic system dimethyl-sulfoxide (DMSO-(CH₃)₂SO)-acetonitrile (AN-CH₃CN) (in a volume ratio of 4:1), which contains LiClO₄ as electrolyte support and chloride salts of CoCl₂, CrCl₃ × 6H₂O, FeCl₂ × 4H₂O, MnCl₂ × 4H₂O and NiCl₂ × 6H₂O. Using MatCalc PC software, based on the CALPHAD method, the structure and characteristics of the HEA system were investigated, and thermodynamic and kinetic criteria were calculated. The modeling process generated in the body-centered-cubic (BCC) or face-centered-cubic (FCC) structures a series of optimal compositions that are appropriate to be used in anticorrosive and tribological applications in a marine environment. Electrochemical measurements were carried out in an aerated artificial seawater solution at ambient temperature. In the experimental media, HEA thin films proved to have good corrosion resistance and were even better than the copper substrate. Corrosion resistance was improved after heat treatment, as shown by polarization and EIS tests. The structure and microstructure of HEA thin films before and after corrosion in artificial seawater were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectrometry (EDS). The XRD data showed no significant changes in the structure of HEA heat-treated thin films after the corrosion in saline media. The data obtained by polarization and ESI are supported by results from SEM-EDS. This complex study reveals that, for HEA thin films, heat treatment leads to an increase in corrosion resistance. So, this finding suggests that thermal annealing is an appropriate method for improving the corrosion performance of HEA thin films.

Lightweight complex concentrated alloys (LWCCA), composed of elements with low density, have become a great area of interest due to the high demand in a large number of applications. Previous research on LWCCAs was focused on high entropy multicomponent alloy systems that provide low density and high capability of solid solution formation. Present research introduces two alloy systems (Al-Cu-Si-Zn-Mg and Al-Mn-Zn-Mg-Si) that contain readily available and inexpensive starting materials and have potential for solid solution formation structures. For the selection of appropriate compositions, authors applied semi-empirical criteria and optimization software. Specialized modeling software (MatCalc) was used to determine probable alloy structures by CALPHAD, non-equilibrium solidification and kinetic simulations. The selected alloys were prepared in an induction furnace. Specimens were heat treated to provide stable structures. Physicochemical, microstructural, and mechanical characterization was performed for the selected alloy compositions. Modeling and experimental results indicated solid solution-based structures in the as-cast and heat-treated samples. Several intermetallic phases were present at higher concentrations than in the conventional alloys. Alloys presented a brittle structure with compression strength of 486–618 MPa and hardness of 268–283 HV. The potential for uniform intermetallic phase distribution in the selected alloys makes them good candidates for applications were low weight and high resistance is required.