The reliable determination of bioapatite crystallinity is of great practical interest, as a proxy to the physico-chemical and microstructural properties, and ultimately, to the integrity of bone materials. Bioapatite crystallinity is used to diagnose pathologies in modern calcified tissues as well as to assess the preservation state of fossil bones. To date, infrared spectroscopy is one of the most applied techniques for bone characterisation and the derived infrared splitting factor (IRSF) has been widely used to practically assess bioapatite crystallinity. Here we thoroughly discuss and revise the use of the IRSF parameter and its meaning as a crystallinity indicator, based on extensive measurements of fresh and fossil bones, virtually covering the known range of crystallinity degree of bioapatite. A novel way to calculate and use the infrared peak width as a suitable measurement of true apatite crystallinity is proposed, and validated by combined measurement of the same samples through X-ray diffraction. The non-linear correlation between the infrared peak width and the derived ISRF is explained. As shown, the infrared peak width at 604 cm⁻¹can be effectively used to assess both the average crystallite size and structural carbonate content of bioapatite, thus establishing a universal calibration curve of practical use.

Nanosized fertilizers are the new frontier of nanotechnology towards a sustainable agriculture. Here, an efficient N-nanofertilizer is obtained by post-synthetic modification (PSM) of nitrate-doped amorphous calcium phosphate (ACP) nanoparticles (NPs) with urea. The unwasteful PSM protocol leads to N-payloads as large as 8.1 w/w%, is well replicated by using inexpensive technical-grade reagents for cost-effective up-scaling and moderately favours urea release slowdown. Using the PSM approach, the N amount is ca. 3 times larger than that obtained in an equivalent one-pot synthesis where urea and nitrate are jointly added during the NPs preparation. In vivo tests on cucumber plants in hydroponic conditions show that N-doped ACP NPs, with half absolute N-content than in conventional urea treatment, promote the formation of an equivalent amount of root and shoot biomass, without nitrogen depletion. The high nitrogen use efficiency (up to 69%) and a cost-effective preparation method support the sustainable real usage of N-doped ACP as a nanofertilizer.

Nanotechnology is emerging as a very promising tool towards more efficient and sustainable practices in agriculture. In this work, we propose the use of non-toxic calcium phosphate nanoparticles doped with urea (U-ACP) for the fertilization of Triticum durum plants. U-ACP nanoparticles present very similar morphology, structure, and composition than the amorphous precursor of bone mineral, but contain a considerable amount of nitrogen as adsorbed urea (up to ca. 6 wt % urea). Tests on Triticum durum plants indicated that yields and quality of the crops treated with the nanoparticles at reduced nitrogen dosages (by 40%) were unaltered in comparison to positive control plants, which were given the minimum N dosages to obtain the highest values of yield and quality in fields. In addition, optical microscopy inspections showed that Alizarin Red S stained nanoparticles were able to penetrate through the epidermis of the roots or the stomata of the leaves. We observed that the uptake through the roots occurs much faster than through the leaves (1 h vs. 2 days, respectively). Our results highlight the potential of engineering nanoparticles to provide a considerable efficiency of nitrogen uptake by durum wheat and open the door to design more sustainable practices for the fertilization of wheat in fields.