Treating large bone defects, known as critical-sized defects (CSDs), is challenging because they are not spontaneously healed by the patient’s body. Due to the limitations associated with conventional bone grafts, bone tissue engineering (BTE), based on three-dimensional (3D) bioprinted scaffolds, has emerged as a promising approach for bone reconstitution and treatment. Bioprinting technology allows for incorporation of living cells and/or growth factors into scaffolds aiming to mimic the structure and properties of the native bone. To date, a wide range of biomaterials (either natural or synthetic polymers), as well as various cells and growth factors, have been explored for use in scaffold bioprinting. However, a key challenge that remains is the fabrication of scaffolds that meet structure, mechanical, and osteoconductive requirements of native bone and support vascularization. In this review, we briefly present the latest developments and discoveries of CSD treatment by means of bioprinted scaffolds, with a focus on the biomaterials, cells, and growth factors for formulating bioinks and their bioprinting techniques. Promising state-of-the-art pathways or strategies recently developed for bioprinting bone scaffolds are highlighted, including the incorporation of bioactive ceramics to create composite scaffolds, the use of advanced bioprinting technologies (e.g., core/shell bioprinting) to form hybrid scaffolds or systems, as well as the rigorous design of scaffolds by taking into account of the influence of such parameters as scaffold pore geometry and porosity. We also review in-vitro assays and in-vivo models to track bone regeneration, followed by a discussion of current limitations associated with 3D bioprinting technologies for BTE. We conclude this review with emerging approaches in this field, including the development of gradient scaffolds, four-dimensional (4D) printing technology via smart materials, organoids, and cell aggregates/spheroids along with future avenues for related BTE.

Injectable hydrogels, as carriers, offer great potential to incorporate cells or growth factors for dental tissue regeneration. Notably, the development of injectable hydrogels with appropriate structures and properties has been a challenging task, leaving much to be desired in terms of cytocompatibility, antibacterial and self-healing properties, as well as the ability to support dental stem cell functions. This paper presents our study on the development of a novel self-cross-linkable hydrogel composed of oxidized alginate and carboxymethyl chitosan and its characterization as a cell carrier for dental enamel regeneration in vitro. Oxidized alginate was synthesized with 60% theoretical oxidation degree using periodate oxidation and characterized by Fourier Transform Infrared spectroscopy, proton nuclear magnetic resonance spectroscopy, and Ultraviolet-visible absorption spectroscopy. Then, hydrogels were prepared at three varying weight ratios of oxidized alginate to carboxymethyl chitosan (4:1, 3:1, and 2:1) through Schiff base reactions, which was confirmed by Fourier Transform Infrared spectroscopy. The hydrogels were characterized in terms of gelation time, swelling ratio, structure, injectability, self-healing, antibacterial properties, and in vitro characterization for enamel regeneration. The results demonstrated that, among the three hydrogels examined, the one with the highest ratio of oxidized alginate (i.e., 4:1) had the fastest gelation time and the lowest swelling ability, and that all hydrogels were formed with highly porous structures and were able to be injected through a 20-gauge needle without clogging. The injected hydrogels could be rapidly reformed with the self-healing property. The hydrogels also showed antibacterial properties against two cariogenic bacteria: Streptococcus mutans and Streptococcus sobrinus. For in vitro enamel regeneration, a dental epithelial cell line, HAT-7, was examined, demonstrating a high cell viability in the hydrogels during injection. Furthermore, HAT-7 cells encapsulated in the hydrogels showed alkaline phosphatase production and mineral deposition, as well as maintaining their round morphology, after 14 days of in vitro culture. Taken together, this study has provided evidence that the oxidized alginate-carboxymethyl chitosan hydrogels could be used as an injectable cell carrier for dental enamel tissue engineering applications.

Background: Bone tissue engineering, based on three-dimensional (3D) printing technology, has emerged as a promising approach to treat bone defects using scaffolds. The objective of this study was to investigate the influence of porosity and internal structure on the mechanical properties of scaffolds. Methods: We fabricated composite scaffolds (which aimed to replicate trabecular bone) from polycaprolactone (PCL) reinforced with 30% (wt.) nano-hydroxyapatite (nHAp) by extrusion printing. Scaffolds with various porosities were designed and fabricated with and without an interlayer offset, termed as staggered and lattice structure, respectively. Mechanical compressive testing was performed to determine scaffold elastic modulus and yield strength. Linear regression was used to evaluate mechanical properties as a function of scaffold porosity. Results: Different relationships between mechanical properties and porosities were noted for the staggered and lattice structures. For elastic moduli, the two relationships intersected (porosity = 55%) such that the lattice structure exhibited higher moduli with porosity values greater than the intersection point; vice versa for the staggered structure. The lattice structure exhibited higher yield strength at all porosities. Mechanical testing results also indicated elastic moduli and yield strength properties comparable to trabecular bone (elastic moduli: 14–165 MPa; yield strength: 0.9–10 MPa). Conclusions: Taken together, this study demonstrates that scaffolds printed from PCL/30% (wt.) nHAp with lattice and staggered structure offer promise for treating trabecular bone defects. This study identified the effect of porosity and internal structure on scaffold mechanical properties and provided suggestions for developing scaffolds with mechanical properties for substituting trabecular bone.

Background: Scaffolds are of great importance in tissue engineering applications as they provide a mechanically supportive environment for cellular activity, which is particularly necessary for hard tissues such as bone. Notably, the mechanical properties of a scaffold vary with differing design parameters such as those related to scaffold height and internal structure. Thus, the present study aimed to explore the relationship between design parameters and mechanical properties of composite polycaprolactone (PCL) and nano-hydroxyapatite (nHAp) scaffolds fabricated by three-dimensional (3D) printing. Methods: We designed and printed scaffolds with different internal structures (lattice and staggered) and varying heights (4, 6, 8 and 10 layers), and consistent porosity (50%) for the purpose of comparison. Then, we examined the scaffold microstructure (pore size and penetration between layers) using scanning electron microscopy (SEM) and mechanical properties (elastic modulus and yield strength) using compressive testing. Results: Our results illustrated that the microstructural parameters were related to scaffold design. At higher heights, pore size increased while penetration between layers decreased; thus, mechanical properties were affected. Results of mechanical testing demonstrated that for lattice scaffolds, elastic modulus was similar for 6 vs 4, and 8 vs 4 layers but ~33% lower for 10 layers vs 4 layers. Similarly, yield strength was comparable for 6 vs 4, and 8 vs 4 layers but ~27% lower for 10 layers vs 4 layers. With staggered scaffolds, when compared to 4-layer results, elastic modulus was similar for 6 layers but was ~43% lower for 8 layers and ~38% lower for 10 layers. Staggered scaffolds had ~38%, ~51%, and ~76% lower yield strength when the number of layers were increased from 4 to 6, 8, and 10 layers, respectively. When comparing lattice and staggered scaffolds with the same layer number, elastic modulus was similar, apart from 8-layer scaffolds where the staggered design was ~42% lower than lattice. Yield strength was similar between 4-layer staggered and lattice scaffolds, while staggered scaffolds with 6, 8, and 10 number of layers showed ~43%, ~45%, ~68% lower strength, respectively, than those found in lattice scaffolds with the same layer numbers. Conclusions: Mechanical properties of 3D printed scaffolds depended on scaffold height for both lattice and staggered internal structures. Staggered scaffolds had lower mechanical properties than the lattice scaffolds with the same height and were more sensitive to the change in scaffold height. Taken together, lattice scaffolds demonstrated the advantages of more stable mechanical properties over staggered scaffolds. Also, scaffolds with lower height were more promising in terms of mechanical properties compared to scaffolds with greater height.

Due to the necessity of prevention of desertification, in range renovation programs, the identification of drought resistant plants and also using multiple purposes of such a plant species is extremely important. The expanse and the protection of medicinal plants can be an income source for local people in desert region and also provide part of pharmacy factory requirements. According to phytogeography classification, Platychaete aucheri belongs to the Khalij-Omani region. This endemic shrub of Iran grows at Fars province (near Jahrom and near Firoozabad), Kerman and Hormozgan. In the present research Platychaete aucheri has been considered in regard to phytochemical characteristic. The aerial parts of Pl. aucheri were collected in the flowering stage. The collected dried samples were extracted by hydrodistillation method. The amount and percentage of essential oil components was 1.76%. 48 components representing 91.3% of the total oil were characterized. The results of chemical components analysis of essential oils has been shown that the main identified components are myrtenol (34.66%), borneol (18.17%), trans-verbenol (5.7%), bornyl acetate (4.31%), cis-verbenol (3.29%) and 1,8-cineole (2.42%), respectively. It seems that borneol, transverbenol and 1,8-cineole play as an anti-quality factor in animal feed. This issue confirms non-palatability of Pl. aucheri in the flowering stage. Hence, one of the rangeland management principles is prevention of entrance non-native and exotic livestock to the rangelands with toxic plants.