Bauxite residue, known as red mud, is a by-product of alumina production using the Bayer process. Currently, its total global storage amounts to over 4.6 billion tons, including about 600 million tons in Russia. The total global storage of red mud occupies large areas, leading to environmental damage and increasing environmental risks. Moreover, it contains a significant amount of sodium, which is easily soluble in subsoil water; therefore, a sustainable approach for comprehensive recycling of red mud is necessary. The bauxite residue contains valuable elements, such as aluminum, titanium, and scandium, which can be recovered using liquid media. In recent years, many methods of recovery of these elements from this waste have been proposed. This paper provides a critical review of hydrometallurgical, solvometallurgical, and complex methods for the recovery of valuable components from red mud, namely, aluminum, titanium, sodium, and rare and rare-earth elements. These methods include leaching using alkaline or acid solutions, ionic liquids, and biological organisms, in addition to red mud leaching solutions by extraction and sorption methods. Advantages and disadvantages of these processes in terms of their environmental impact are discussed.

The chemical and mineral composition of the red mud from the Ural Aluminum Plant were studied by XRF, XRD, and Mössbauer spectroscopy. Experiments on reductive smelting of red mud were carried out in a range of temperatures (1650–1750 °C) to recover iron from the aluminum production waste with maximum efficiency. It was found that it is possible to obtain pig iron with a high content of titanium, phosphorus, and vanadium, and low sulfur content. The efficiency of iron recovery at 1750 °C was found to be around 98%. Thermodynamic calculations were carried out to assist in finding the optimal conditions for the process (e.g., carbon content, furnace temperature, slag liquidus temperature). It was also found that the pig iron phase obtained at 1650 to 1700 °C is not separated from the slag phase into ingot compared with the sample obtained at 1750 °C. Pig iron obtained at 1750 °C can be used to produce molds for the steel-casting equipment.

Managing red mud (RM), a solid waste byproduct of the alumina recovery process, is a serious ecological and environmental issue. With ~150 million tons/year of RM being generated globally, nearly 4.6 billion tons of RM are presently stored in vast waste reserves. RM can be a valuable resource of metals, minor elements, and rare earth elements. The suitability of RM as a low-grade iron resource was assessed in this study. The utilization of RM as a material resource in several commercial, industrial operations was briefly reviewed. Key features of iron recovery techniques, such as magnetic separation, carbothermal reduction, smelting reduction, acid leaching, and hydrothermal techniques were presented. RMs from different parts of the globe including India, China, Greece, Italy, France, and Russia were examined for their iron recovery potential. Data on RM composition, iron recovery, techniques, and yields was presented. The composition range of RMs examined were: Fe₂O₃: 28.3–63.2 wt.%; Al₂O₃: 6.9–26.53 wt.%; SiO₂: 2.3–22.0 wt.%; Na₂O: 0.27–13.44 wt.%; CaO: 0.26–23.8 wt.%; Al₂O₃/SiO₂: 0.3–4.6. Even with a high alumina content and high Al₂O₃/SiO₂ ratios, it was possible to recover iron in all cases, showing the significant potential of RM as a secondary resource of low-grade iron.

The results of experiments on the use of red mud in traditional pyrometallurgical processes and plants are presented. The red muds of the Ural Aluminum Plant (UAZ, Kamensk-Ural’skii) and the Alyum Pla

Red mud is a by-product of alumina production from bauxite ore by the Bayer method, which contains considerable amounts of valuable components such as iron, aluminum, titanium, and scandium. In this study, an approach was applied to extract iron, i.e., carbothermic reduction roasting of red mud with sodium and potassium carbonates followed by magnetic separation. The thermodynamic analysis of iron and iron-free components’ behavior during carbothermic reduction was carried out by HSC Chemistry 9.98 (Outotec, Pori, Finland) and FactSage 7.1 (Thermfact, Montreal, Canada; GTT-Technologies, Herzogenrath, Germany) software. The effects of the alkaline carbonates’ addition, as well as duration and temperature of roasting on the iron metallization degree, iron grains’ size, and magnetic separation process were investigated experimentally. The best conditions for the reduction roasting were found to be as follows: 22.01% of K₂CO₃ addition, 1250 °C, and 180 min of duration. As a generalization of the obtained data, the mechanism of alkaline carbonates’ influence on iron grain growth was proposed.

Red mud is a hazardous waste of the alumina industry that contains high amounts of iron, aluminum, titanium and rare-earth elements (REEs). One of the promising methods for the extraction of iron from red mud is carbothermic reduction with the addition of sodium salts. This research focuses on the process of hydrochloric high-pressure acid leaching using 10 to 20% HCl of two samples of non-magnetic tailings obtained by 60 min carbothermic roasting of red mud at 1300 °C and the mixture of 84.6 wt.% of red mud and 15.4 wt.% Na₂SO₄ at 1150 °C, respectively, with subsequent magnetic separation of metallic iron. The influence of temperature, leaching duration, solid-to-liquid-ratio and acid concentration on the dissolution behavior of Al, Ti, Mg, Ca, Si, Fe, Na, La, Ce, Pr, Nd, Sc, Zr was studied. Based on the investigation of the obtained residues, a mechanism for passing valuable elements into the solution was proposed. It has shown that 90% Al, 91% Sc and above 80% of other REEs can be dissolved under optimal conditions; Ti can be extracted into the solution or the residue depending on the leaching temperature and acid concentration. Based on the research results, novel flowsheets for red mud treatment were developed.