Developing superior properties of epoxy resin composites with high fire resistance, light smoke, and low toxicity has been the focus of the research in the flame-retardant field. In particular, it is essential to decrease the emissions of toxic gases and smoke particles generated during the thermal decomposition of epoxy resin (EP) to satisfy the industrial requirements for environmental protection and safety. Consequently, the PZS@ZIF-67 composite was designed and synthesized by employing the hydroxyl group-containing polyphosphazene (poly(cyclotriphosphazene-co-4,4′-dihydroxydiphenylsulfone), PZS) as both the interfacial compatibility and an in situ template and the ZIF-67 nanocrystal as a nanoscale coating and flame-retardant cooperative. ZIF-67 nanocrystal with multidimensional nanostructures was uniformly wrapped on the surface of PZS microspheres. Subsequently, the acquired PZS@ZIF-67 composite was incorporated into the epoxy resin to prepare composite samples for the study of their fire safety, toxicity suppression, and mechanical performance. Herein, the EP/5% PZS@ZIF-67 passed the V-0 rating in a UL-94 test with a 31.9% limit oxygen index value. More precisely, it is endowed with a decline of 51.08%, 28.26%, and 37.87% of the peak heat release rate, the total heat release, and the total smoke production, respectively. In addition, the unique structure of PZS@ZIF-67 microsphere presented a slight impact on the mechanical properties of EP composites at low loading. The PZS@ZIF-67 possible flame-retardant mechanism was speculated based on the analysis of the condensed phase and the gas phase of EP composites.

A new strategy for the preparation of an integrated three-source intumescent flame retardant (IFR) has been developed to improve the flame-retardant and smoke suppression performance of epoxy resin (EP) with a synergistic flame retardant effect. Herein, the synthesis of a macromolecular spirocyclic phosphorus/nitrogen-containing IFR poly sulfonamide spirocyclic pentaerythritol bisphosphonate (SAPC) is reported via a two-step method that uses pentaerythritol, phosphorus oxychloride and sulfonamide (SAA) as raw materials. Subsequently, the SAPC was incorporated into EP to prepare the composite to investigate its thermal stability, flame retardancy, and smoke suppression performance. Herein, a differential scanning calorimetry (DSC) analysis showed that the addition of SAPC increased the glass transition temperature (T_g) of the composite. Cone test results indicated that the incorporation of 8 wt % SAPC significantly improved the flame-retardant performance for the composite, with a 43.45% decrease in peak of heat release rate, a 28.55% reduction in total heat release, and a 30.04% decrease in total smoke release. Additionally, the composite received the V-0 rating in a UL-94 vertical burning test, accompanied by the “blowout” phenomenon. After the addition of SAPC, the amount of flammable gas products from the EP composite decomposition was obviously suppressed, and the amount of non-flammable as was increased. All of this suggests a good dilution role of SAPC. There are enough reasons to believe that the enhanced flame-retardant and toxicity suppression performance for the EP composite can be attributed to the good coordination of carbonization agent, acid source, and blowing agent in the SAPC structure.

Derivatives of 3,9-dichloro-2,4,8,10-tetraoxa-3,9-diphosphaspiro-[5,5]undecane-3,9-dioxide (SPDPC) are of increasing interest as flame retardants for polymeric materials. In addition, SPDPC is also an important intermediate for the preparation of intumescent flame retardants (IFRs). However, low efficiency and undesirable dispersion are two major problems that seriously restrain the application of IFRs as appropriate flame retardants for polymer materials. Usually, the functionalization or modification of SPDPC is crucial to acquiring high-performance polymer composites. Here, a small molecule spirocyclic flame retardant diphenylimidazole spirocyclic pentaerythritol bisphosphonate (PIPC) was successfully prepared through the substitution reaction between previously synthesized intermediate SPDPC and 2-phenylimidazole (PIM). Phenyl group and imidazole group were uniformly anchored on the molecular structure of SPDPC. This kind of more uniform distribution of flame retardant groups within the epoxy matrix resulted in a synergistic flame retardant effect and enhanced the strength of char layers to the epoxy composites, when compared to the unmodified epoxy. The sample reached a limiting oxygen index (LOI) of 29.7% and passed with a V-0 rating in the UL 94 test with the incorporation of only 5 wt% of as-prepared flame retardant PIPC. Moreover, its peak of heat release rate (pHRR) and total heat release (THR) decreased by 41.15% and 21.64% in a cone calorimeter test, respectively. Furthermore, the addition of PIPC has only slightly impacted the mechanical properties of epoxy composites with a low loading.

The flammability of epoxy resins and knowing how to achieve curing are particularly important factors during use. A novel approach for enhancing the fire resistance and reducing the smoke emission of epoxy resin during the curing process is suggested, which involves the utilization of a three-source integrated polymerization intumescent flame-retardant. In this study, the synthesis of poly 4,4-diaminodiphenylsulfone spirocyclic pentaerythritol bisphosphonate (PCS) is achieved through using solution polymerization, utilizing 4,4′-diaminodiphenylsulfone (DDS) and spirocyclic pentaerythritol bisphosphorate disphosphoryl chloride (SPDPC) as initial components. Following that, the EP underwent the inclusion of PCS to examine its resistance to heat, its ability to prevent flames, its effectiveness in reducing smoke and its curing effect. Compared to the unmodified epoxy resin, the addition of PCS can not only cure the epoxy resin, but also decompose before the epoxy resin and has a good carbonization effect. With the addition of 7 wt.% PCS, the LOI value can achieve 31.2% and successfully pass the UL-94 test with a V-0 rating. Moreover, the cone calorimeter experiment demonstrated a noteworthy decline of 59.7% in the maximum heat release rate (pHRR), 63.7% in overall heat release (THR), and 42.3% in total smoke generation (TSP). Based on the examination of TG-FTIR and SEM findings, there is ample evidence to suggest that PCS, functioning as a phosphorus-nitrogen intumescent flame-retardant that combines three origins, has the potential to exhibit a favorable flame-retardant impact in both its gas and condensed phases.

TATB and TATB-d6 were synthesized using phloroglucinol as raw material. Their molecular structure and micromorphology of them were well characterized by FTIR, NMR spectroscopy, XRD and FE-SEM. The thermal behaviors of these compounds were studied with TG-DSC, and the non-isothermal kinetic decomposition parameters of the two compounds were gained using the method of Friedman (FM). The apparent activation energy value of TATB-d6 was larger than that of TATB, which indicated the heat stabilization of deuterated TATB particles was improved. Finally, the thermal detonation critical temperatures of these two products were also calculated and discussed.

The metal/fluoropolymer reactive materials (RMs) have been widely studied in the past years. Almost no reported Al/THV RMs, which was prepared in this work, shows better mechanical properties than well researched Al/PTFE. In addition, the mechanical properties and reaction characteristics of Al/THV composites with two particle sizes and different contents of aluminium particles were tested. The effects of particle size and content of aluminium on Al/THV RMs were analysed. The result shows that Al/THV composite with high contents of 4 μm Al particles shows better mechanical properties and reaction characteristics than the other Al/THV composites. Besides, the low impact-induced reaction percentage of Al/THV (35/65) composite under ~7000 s^-1 compression was explained by the low combustion velocity and plasticity.