Different loadings of organo-montmorillonite (OMMT) were mixed with ultra-high molecular weight polyethylene (UHMWPE)/polypropylene (70/30) composites under elongation flow. Results showed that ideal dispersion of OMMT nanoparticles could be achieved and most OMMTs intercalated and exfoliated effectively. However, the layer spacing of OMMT decreased with the increase in the content of OMMT. UHMWPE was surrounded by the OMMT layers, and its shape evolved from a compatible phase to a sphere. OMMT caused heterogeneous nucleation in the blends, leading to a high crystallisation temperature. Meanwhile, the intercalated and exfoliated OMMTs promoted the motion of polymer chains, and inhibited the crystallisation process of UHMWPE in the composites. The crystallinity of UHMWPE with 5% OMMT markedly decreased from 48.39% to 41.46%. Various rheological analyses confirmed that the complex viscosity of composites and the storage modulus decreased first and then increased with the increase in the content of OMMT. UHMWPE/PP with 5% OMMT exhibited the ideal mobility.

A simple approach to decorate multi-walled carbon nanotube (MWCNT)–reduced graphene oxide (RGO) hybrid nanoparticles with zinc oxide (ZnO) nanorods is developed to improve the electrical and mechanical properties of poly(vinyl chloride) (PVC)/MWCNT–RGO composites. The ZnO nanorods act as “joint” in three-dimensional (3D) MWCNT–RGO networks and the hybrid particles strongly interact with PVC chains via p-π stacking, hydrogen bonds, and electrostatic interactions, which we confirmed by scanning electron microscopy (SEM) and Raman analysis. By introducing the ZnO nanorods, the RGO–ZnO–MWCNT hybrid particles increased 160% in capacitance compared with MWCNT–RGO hybrids. Moreover, the addition of RGO–ZnO–MWCNT to PVC resulted in the mechanical properties of PVC being enhanced by 30.8% for tensile strength and 60.9% for Young’s modulus at the loadings of 2.0 weight percent (wt.%) and 1.0 wt.%, respectively. Meanwhile, the electrical conductivity of PVC increased by 11 orders of magnitude, from 1 × 10⁻¹⁵ S/m to 1 × 10⁻⁴ S/m for MWCNT–ZnO–RGO loading at 5.0 wt.%.

A leaf-inspired double-layer membrane was designed, exhibiting 99.3% solar reflectivity and ∼95% mid-infrared emissivity. It remained stable under 7000 MJ m ⁻² ultraviolet radiation, presenting a new strategy for passive radiative cooling.