This study investigated the efficiency of chitosan/polyethylene oxide (PEO)-based nanofibers with incorporated bioactive glass particles as a coating for titanium alloy, in order to improve the bacteriostatic behavior and, concurrently, promote the production of mineralized tissue. Nanofibers with and without bioglass powder were fabricated by electrospinning technique and characterized using several microscopic and spectroscopic techniques in order to study their morphological and physiochemical properties. Subsequently, the substrates were tested in vitro against Staphylococcus epidermidis and SaOS-2 human osteosarcoma cell line. After in vitro testing, viability and CFU counting assays combined with fluorescence microscopy showed a clear decrease in bacterial growth on all substrates with increasing time. However, this trend was stronger for substrates coated with nanofibers. Formation of mineralized matrix upon exposure to osteoblasts was confirmed by means of SEM/EDX and the content/distribution of osteocalcin and osteopontin estimated by fluorescence microscopy. Incorporation of bioglass promoted biomineralization and stimulated osteoblasts to produce a higher amount of bone extracellular matrix. The present results suggest that a chitosan/PEO/bioactive glass nanofiber composite applied as coating on titanium alloys could concurrently improve antibacterial and osteoconductive properties and could be a potential candidate for dental and orthopedic applications.

Centrifugal spinning, which is a high-productivity fiber fabrication technique, was used to produce a value-added product from recycled poly(ethylene terephthalate) (rPET). In the present study, rPET fibers, with fiber diameters ranging from submicron to micrometer in scale, were fabricated by spinning a solution of rPET in a mixture of dichloromethane and trifluoroacetic acid. The influence of the polymer solution concentration (the viscosity), the rotational speed of the spinneret, and the inner diameter of the needles on the formation and morphology and mechanical properties of the fibers were examined through scanning electron microscopy and using a tensile testing machine. The thermal behaviors of fibrous mats with various average diameters were also investigated through differential scanning calorimetry. The smoothest and smallest fibers, with an average diameter of 619 nm, were generated using an rPET solution of 10 wt % under a rotation speed of 15,000 rpm using needles having an inner diameter of 160 μm. The fibrous mats have an average tensile strength and modulus of 4.3 MPa and 34.4 MPa, respectively. The productivity and the mechanical properties indicate that centrifugal spinning is an effective technique to fabricate high-value product from rPET.

The demand for an efficient oil sorbent with high sorption capacity, low cost, scalable fabrication, and high selectivity for the cleanup of spreading oil on water is increasingly urgent due to the frequent occurrence of oil spill accidents in seawater all over the world. In this study, porous polystyrene (PS) fibers with high hydrophobicity and superoleophilicity were directly fabricated by a centrifugal spinning method (CS). The effect of solvents, tetrahydrofuran (THF), and dimethylformamide (DMF) on the morphology and porous structure of the polystyrene fibers was evaluated by using scanning electron microscopy and nitrogen adsorption–desorption experiments. The formation mechanism for the porous structure on the fibers was also evaluated. The oil sorption capacities of the PS fibers for silicon oil, pump oil, and vegetable oil were investigated. The highest oil sorption capacity was found in PS fibers fabricated from PS solution with a THF/DMF weight ratio of 1/3, which exhibited the highest specific surface area, pore volume, and porosity. The high productivity and highly porous structure of PS fibers indicate that CS is a promising method to fabricate porous fibers for the cleanup of oil spills.

Quickly updatable hologram images using photorefractive (PR) polymer composite based on poly(N-vinyl carbazole) (PVCz) is presented. PVCz is one of the pioneer materials of photoconductive polymers. PR polymer composite consists of 44 wt % of PVCz, 35 wt % of 4-azacycloheptylbenzylidene-malonitrile (7-DCST) as a nonlinear optical dye, 20 wt % of carbazolylethylpropionate (CzEPA) as a photoconductive plasticizer and 1 wt % of 2,4,7-trinitro-9-fluorenone (TNF) as a sensitizer. PR composite gives high diffraction efficiency of 68% at E = 45 V μm⁻¹. Response speed of optical diffraction is the key parameter for real-time 3D holographic display. The key parameter for obtaining quickly updatable holographic images is to control the glass transition temperature lower enough to enhance chromophore orientation. Object image of the reflected coin surface recorded with reference beam at 532 nm (green beam) in the PR polymer composite is simultaneously reconstructed using a red probe beam at 642 nm. Instead of using a coin object, an object image produced by a computer was displayed on a spatial light modulator (SLM) and used for the hologram. The reflected object beam from an SLM was interfered with a reference beam on PR polymer composite to record a hologram and simultaneously reconstructed by a red probe beam.