This study investigated the efficiency of chitosan/polyethylene oxide (PEO)-based nanofibers with incorporated bioactive glass particles as a coating for titanium alloy, in order to improve the bacteriostatic behavior and, concurrently, promote the production of mineralized tissue. Nanofibers with and without bioglass powder were fabricated by electrospinning technique and characterized using several microscopic and spectroscopic techniques in order to study their morphological and physiochemical properties. Subsequently, the substrates were tested in vitro against Staphylococcus epidermidis and SaOS-2 human osteosarcoma cell line. After in vitro testing, viability and CFU counting assays combined with fluorescence microscopy showed a clear decrease in bacterial growth on all substrates with increasing time. However, this trend was stronger for substrates coated with nanofibers. Formation of mineralized matrix upon exposure to osteoblasts was confirmed by means of SEM/EDX and the content/distribution of osteocalcin and osteopontin estimated by fluorescence microscopy. Incorporation of bioglass promoted biomineralization and stimulated osteoblasts to produce a higher amount of bone extracellular matrix. The present results suggest that a chitosan/PEO/bioactive glass nanofiber composite applied as coating on titanium alloys could concurrently improve antibacterial and osteoconductive properties and could be a potential candidate for dental and orthopedic applications.

Centrifugal spinning, which is a high-productivity fiber fabrication technique, was used to produce a value-added product from recycled poly(ethylene terephthalate) (rPET). In the present study, rPET fibers, with fiber diameters ranging from submicron to micrometer in scale, were fabricated by spinning a solution of rPET in a mixture of dichloromethane and trifluoroacetic acid. The influence of the polymer solution concentration (the viscosity), the rotational speed of the spinneret, and the inner diameter of the needles on the formation and morphology and mechanical properties of the fibers were examined through scanning electron microscopy and using a tensile testing machine. The thermal behaviors of fibrous mats with various average diameters were also investigated through differential scanning calorimetry. The smoothest and smallest fibers, with an average diameter of 619 nm, were generated using an rPET solution of 10 wt % under a rotation speed of 15,000 rpm using needles having an inner diameter of 160 μm. The fibrous mats have an average tensile strength and modulus of 4.3 MPa and 34.4 MPa, respectively. The productivity and the mechanical properties indicate that centrifugal spinning is an effective technique to fabricate high-value product from rPET.

The demand for an efficient oil sorbent with high sorption capacity, low cost, scalable fabrication, and high selectivity for the cleanup of spreading oil on water is increasingly urgent due to the frequent occurrence of oil spill accidents in seawater all over the world. In this study, porous polystyrene (PS) fibers with high hydrophobicity and superoleophilicity were directly fabricated by a centrifugal spinning method (CS). The effect of solvents, tetrahydrofuran (THF), and dimethylformamide (DMF) on the morphology and porous structure of the polystyrene fibers was evaluated by using scanning electron microscopy and nitrogen adsorption–desorption experiments. The formation mechanism for the porous structure on the fibers was also evaluated. The oil sorption capacities of the PS fibers for silicon oil, pump oil, and vegetable oil were investigated. The highest oil sorption capacity was found in PS fibers fabricated from PS solution with a THF/DMF weight ratio of 1/3, which exhibited the highest specific surface area, pore volume, and porosity. The high productivity and highly porous structure of PS fibers indicate that CS is a promising method to fabricate porous fibers for the cleanup of oil spills.

The present work investigated the effect of Polylactic acid (PLA) fibers produced by centrifugal spinning with incorporated BaTiO₃ particles to improve their bacteriostatic behavior. The PLA matrix and three composites, presenting three different amounts of fillers, were subjected to UV/O₃ treatment monitoring the possible modifications that occurred over time. The morphological and physical properties of the surfaces were characterized by different microscopic techniques, contact angle, and surface potential measurements. Subsequently, the samples were tested in vitro with human dermal fibroblasts (HDF) to verify the cytotoxicity of the substrates. No significant differences between the PLA matrix and composites emerged; the high hydrophobicity of the fibers, derived by the polymer structure, represented an obstacle limiting the fibroblast attachment. Samples underwent bacterial exposure (Staphylococcus epidermidis) for 12 and 24 h. Increasing the concentration of BT, the number of living bacteria and their distribution decreased in comparison with the PLA matrix suggesting an effect of the inorganic filler, which generates a neutralization effect leading to reactive oxygen species (ROS) generation and subsequently to bacterial damages. These results suggest that the barium titanate (BT) fillers clearly improve the antibacterial properties of PLA fibers after aging tests made before bacterial exposure, representing a potential candidate in the creation of composites for medical applications.