Fatigue crack in rails and cyclic-loaded train parts is a contributory factor in multiple railroad accidents. We address the problem of crack detection and measurement at early stages, when total failure has not yet occurred. We propose to combine acoustic emission (AE) testing for prediction of crack growth with digital image correlation (DIC) for its accurate quantitative characterization. In this study, we imitated fatigue crack appearance and growth in samples of railway rail and two train parts by cyclic loading, and applied these two techniques for inspection. Experimental results clearly indicate the efficiency of AE in the early detection of fatigue cracks, and excellent DIC capabilities in terms of geometrical measurements. Combination of these techniques reveals a promising basis for real-time and non-destructive monitoring of rails and train parts.

This paper presents a study of acoustic emission (AE) during the deformation of dissimilar welded joints of austenitic steel to pearlitic steel. One of the specific problems in these welded joints is the presence of decarburized and carbide diffusion interlayers, which intensively increase in width during long-term high-temperature operation. The presence of wide interlayers negatively affects the mechanical properties of welded joints. Moreover, welded defects are difficult to diagnose in welded joints containing interlayers: due to the high structural heterogeneity, interlayers create structural noises that can hinder the detection of defects such as cracks, pores, or a lack of penetration. The AE method may become a complex decision for diagnosing dissimilar welded joints due to applicability to the testing of heterogenic materials with a complex microstructure. Specimens cut from dissimilar welded joints of austenitic steel to pearlitic steel were tested by tension to rupture, with parallel AE data registration. According to the research results, the characteristic features of the AE were revealed for specimens containing defects in the form of lack of penetration as well as for specimens with diffusion interlayers. The results obtained show that the AE method can be used to test both typical welding defects and diffusion interlayers in welded joints of steels of different structural classes.

In this study, we investigated defect detection in dissimilar welded joints by the acoustic emission (AE) method. The study objects were carbide and decarburized interlayers, which are formed at the fusion boundary between austenitic and pearlitic steels. Diffusion interlayers, as a structural defect, usually have microscopic dimensions and cannot be detected using conventional non-destructive testing (NDT) methods. In this regard, the AE method is a promising approach to diagnose metal objects with a complex structure and to detect microscopic defects. In this paper, the AE signatures obtained from testing defect-free specimens and specimens with diffusion interlayers are analyzed. We found that the AE signature for defective and defect-free welded joints has significant differences, which makes it possible to identify descriptors corresponding to the presence of diffusion interlayers in dissimilar welded joints.

Acoustic emission (AE) testing is traditionally carried out on non-operating objects. Such requirement is associated both with the Kaiser effect, leading to the necessity for exceeding the test load above the working one and with a high level of noise during object operation. However, AE testing could be performed under operating conditions, if the AE data acquisition period is increased and a specialized method is developed, which should take account of the effect of various noise, features of the object loading under operating conditions, the effect of damaging factors and possible destruction mechanisms. This paper investigates the possibility to carry out structural health monitoring (SHM) of hydrotreaters, highway bridges, high-temperature pipelines, gas adsorbers, roller bearings of rotary kilns and draglines on the basis of AE method. Architecture of SHM-system and specific data analysis procedures are proposed.

We address non-contact detection of defects in the railway rails under their dynamic loading and propose to combine digital image correlation (DIC) and finite element modeling (FEM). We show that accurate model of defect-free rail operating at the same loading conditions as the inspected one provides a reliable reference for experimental data. In this study, we tested the rail samples with artificial and fatigue defects under cyclic loading, calculated displacement and stress distributions at different locations of the cracks via DIC and validated the obtained results by FEM. The proposed DIC-FEM approach demonstrates high sensitivity to fatigue cracks and can be effectively used for remote control of rails as well as for non-destructive testing of various other objects operating under dynamic loads.

The article is devoted to the organization of the structural health monitoring of a walking dragline excavator using the acoustic emission (AE) method. Since the dragline excavator under study is a large and noisy industrial facility, preliminary prospecting researches were carried out to conduct effective control by the AE method, including the study of AE sources, AE waveguide, and noise parameters analysis. In addition, AE filtering methods were improved. It is shown that application of the developed filtering algorithms allows to detect AE impulses from cracks and defects against a background noise exceeding the useful signal in amplitude and intensity. Using the proposed solutions in the monitoring of a real dragline excavator during its operation made it possible to identify a crack in one of its elements (weld joint in a dragline back leg).