PEEK-OPTIMA^™ (Invibio Ltd, UK) has been considered as an alternative joint arthroplasty bearing material due to its favourable mechanical properties and the biocompatibility of its wear debris. In this study, the potential to use injection moulded PEEK-OPTIMA^™ as an alternative to cobalt chrome in the femoral component of a total knee replacement was investigated in terms of its wear performance. Experimental wear simulation of three cobalt chrome and three PEEK-OPTIMA^™ femoral components articulating against all-polyethylene tibial components was carried out under two kinematic conditions: 3 million cycles under intermediate kinematics (maximum anterior-posterior displacement of 5 mm) followed by 3 million cycles under high kinematic conditions (anterior-posterior displacement 10 mm). The wear of the GUR1020 ultra-high-molecular-weight polyethylene tibial components was assessed by gravimetric analysis; for both material combinations under each kinematic condition, the mean wear rates were low, that is, below 5 mm³/million cycles. Specifically, under intermediate kinematic conditions, the wear rate of the ultra-high-molecular-weight polyethylene tibial components was 0.96 ± 2.26 mm³/million cycles and 2.44 ± 0.78 mm³/million cycle against cobalt chrome and PEEK-OPTIMA^™ implants, respectively (p = 0.06); under high kinematic conditions, the wear rates were 2.23 ± 1.85 mm³/million cycles and 4.44 ± 2.35 mm³/million cycles, respectively (p = 0.03). Following wear simulation, scratches were apparent on the surface of the PEEK-OPTIMA^™ femoral components. The surface topography of the femoral components was assessed using contacting profilometry and showed a statistically significant increase in measured surface roughness of the PEEK-OPTIMA^™ femoral components compared to the cobalt chrome implants. However, this did not appear to influence the wear rate, which remained linear over the duration of the study. These preliminary findings showed that PEEK-OPTIMA^™ gives promise as an alternative bearing material to cobalt chrome alloy in the femoral component of a total knee replacement with respect to wear performance.

PEEK-OPTIMA™ is being considered as an alternative bearing material to cobalt chrome in the femoral component of total knee replacement to provide a metal-free implant. The aim of this study was to investigate the influence of lubricant temperature (standard rig running and elevated temperature (~36 °C)) on the wear of a UHMWPE-on-PEEK OPTIMA™ bearing couple using different lubricant protein concentrations (0%, 2%, 5%, 25% and 90% bovine serum) in a simple geometry pin-on-plate configuration. Friction was also investigated under a single temperature condition for different lubricant protein concentrations. The studies were repeated for UHMWPE-on-cobalt chrome in order to compare relationships with temperature (wear only) and lubricant protein concentration (wear and friction). In low lubricant protein concentrations (≤ 5%) there was no influence of temperature on the wear factors of UHMWPE-on-PEEK. With 25% bovine serum, the wear factor of UHMWPE-on-PEEK reduced by half at elevated temperature. When tested in high protein concentration (90% serum), there was no influence of temperature on the wear factor of UHMWPE-on-PEEK. These temperature dependencies were not the same for UHMWPE-on-cobalt chrome. For both material combinations, there was a trend of decreasing friction with increasing protein concentration once protein was present in the lubricant. This study has shown the importance of the selection of appropriate test conditions when investigating the wear and friction of different materials, in order to minimise test artefacts such as polymer transfer, and protein precipitation and deposition.

PEEK-OPTIMA™ is being considered as an alternative to cobalt chrome (CoCr) in the femoral component of total knee replacements. To date, investigations of ultra-high molecular weight polyethylene (UHMWPE)-on-PEEK have shown an equivalent wear rate to conventional implant materials under standard conditions. In this study, the third body wear performance of UHMWPE-on-PEEK was directly compared to UHMWPE-on-CoCr in a series of pin-on-plate studies using two approaches for third body damage. Damage simulation with particles of bone cement showed a significant (p < 0.001), four-fold increase in the mean surface roughness of PEEK plates compared to CoCr. However, wear simulation against the damaged plates showed no significant difference in the wear of UHMWPE pins against the different materials (p = 0.59), and a polishing effect by the pin against the PEEK plates was observed. Scratching PEEK and CoCr counterfaces with a diamond stylus to create scratches representative of severe third body damage (4 µm lip height) resulted in a significantly higher (p = 0.01) wear of UHMWPE against CoCr compared to PEEK and again, against PEEK plates, polishing by the UHMWPE pin led to a reduction in scratch lip height. This study shows that in terms of its wear performance under third body wear/damage conditions, UHMWPE-on-PEEK differs from conventional knee replacement materials.

This study investigated the fixation of a cemented PEEK femoral TKA component. PEEK and CoCr implants were subjected to a walking gait cycle for 10 million cycles (MC), 100,000 cycles or 0 cycles (unloaded control). A method was developed to assess the fixation at the cement–implant interface, which exposed the implants to a fluorescent penetrant dye solution. The lateral condyles of the implants were then sectioned and viewed under fluorescence to investigate bonding at the cement–implant interface and cracking of the cement mantle. When tested for 100,000 cycles, debonding of the cement–implant interface occurred in both PEEK (61%) and CoCr (13%) implants. When the duration of testing was extended (10 MC), the percentage debonding was further increased for both materials to 88% and 61% for PEEK and CoCr, respectively. The unloaded PEEK specimens were 79% debonded, which suggests that, when PEEK femoral components are cemented, complete bonding may never occur. Analysis of cracks in the cement mantle showed an absence of full-thickness cracks in the unloaded control group. For the 100,000-cycle samples, on average, 1.3 and 0.7 cracks were observed for PEEK and CoCr specimens, respectively. After 10 MC, these increased to 24 for PEEK and 19 for CoCr. This was a preliminary study with a limited number of samples investigated, but shows that, after 10 MC under a walking gait, substantial debonding was visible for both PEEK and CoCr implants at the cement–implant interface and no significant difference in the number of cement cracks was found between the two materials.

Calcium sulfate bone void fillers are increasingly being used for dead space management in infected arthroplasty revision surgery. The presence of these materials as loose beads close to the bearing surfaces of joint replacements gives the potential for them to enter the joint becoming trapped between the articulating surfaces; the resulting damage to cobalt chrome counterfaces and the subsequent wear of ultra-high-molecular-weight polyethylene is unknown. In this study, third-body damage to cobalt chrome counterfaces was simulated using particles of the calcium sulfate bone void fillers Stimulan ^® (Biocomposites Ltd., Keele, UK) and Osteoset ^® (Wright Medical Technology, TN, USA) using a bespoke rig. Scratches on the cobalt chrome plates were quantified in terms of their density and mean lip height, and the damage caused by the bone void fillers was compared to that caused by particles of SmartSet GMV PMMA bone cement (DePuy Synthes, IN, USA). The surface damage from Stimulan ^® was below the resolution of the analysis technique used; SmartSet GMV caused 0.19 scratches/mm with a mean lip height of 0.03 µm; Osteoset ^® led to a significantly higher number (1.62 scratches/mm) of scratches with a higher mean lip height (0.04 µm). Wear tests of ultra-high-molecular-weight polyethylene were carried out in a six-station multi-axial pin on plate reciprocating rig against the damaged plates and compared to negative (highly polished) and positive control plates damaged with a diamond stylus (2 µm lip height). The wear of ultra-high-molecular-weight polyethylene was shown to be similar against the negative control plates and those damaged with third-body particles; there was a significantly higher ( p < 0.001) rate of ultra-high-molecular-weight polyethylene wear against the positive control plates. This study showed that bone void fillers of similar composition can cause varying damage to cobalt chrome counterfaces. However, the lip heights of the scratches were not of sufficient magnitude to increase the wear of ultra-high-molecular-weight polyethylene above that of the negative controls.