The main trough is a part of the blast furnace process for hot metal and molten slag transportation from the tap hole to the torpedo, and mechanical erosion of the trough is an important reason for a short life of a campaign. This article employed OpenFoam code to numerically study and analyze velocity, temperature and wall shear stress of the fluids in the main trough during a full tapping process. In the code, a three-dimensional transient mass, momentum and energy conservation equations, including the standard k-ε turbulence model, were developed for the fluid in the trough. Temperature distribution in refractory is solved by the Fourier equation through conjugate heat transfer with the fluid in the trough. Change velocities of the fluid during the full tapping process are exactly described by a parabolic equation. The investigation results show that there are strong turbulences at the area of hot metal’s falling position and the turbulences have influence on velocity, temperature and wall shear stress of the fluid. With the increase of the angle of the tap hole, the wall shear stress increases. Mechanical erosion of the trough has the smallest value and the campaign of the main trough is estimated to expand over 5 days at the tap hole angle of 7°.

Copper staves have been widely applied in large blast furnaces especially those whose inner volumes exceed 2000 m³ due to high cooling capacity. In the past decade, copper staves suffered severe damages in some blast furnaces, which not only shortened their campaign lives, but also caused huge economic losses. In order to make out this phenomenon, the damage mechanism of copper staves was investigated via analyzing the chemical composition, thermal conductivity, metallographic aspects and microstructure in this paper. As a result, the working state was more likely to damage copper staves instead of their materials. At the beginning, the poor quality of the coke and the large bosh angle promoted the development of edge airflow, which intensified the erosion of refractory materials, resulting in the fall-off of slag crusts and damage of cooling water pipes. After repair, the cooling capacity of copper staves still declined, causing the temperature to rise easily; consequently, hydrogen attack happened when the temperature reached 370 °C, which degraded the performance of copper staves. Therefore, copper staves were worn too quickly to form slag crusts, which finally failed under the hydrogen attack and the scouring of the edge airflow at high temperatures.

The main trough of a blast furnace (BF) is a main passage for hot metal and molten slag transportation from the taphole to the torpedo and the slag handling. Its appropriate working status and controlled erosion ensure a safe, stable, high-efficiency and low-cost continuous production of hot metal. In this work, the tapping process of a main trough of a BF in the east of China was numerically studied with the help of a CFD library written in C++, called OpenFOAM, based on the use of the Finite Volume Method (FVM). The results show that turbulence intensity downstream of the hot metal impact position becomes weaker and the turbulence area becomes larger in the main trough. During the tapping, thermal stress of wall refractory reaches the maximum value of $1{.7\times 10}^7$ Pa at the 4 m position in the main trough. Furthermore, baffles in the main trough placed between 5.8 m and 6.2 m were found to control and reduce the impact of the turbulence on the refractory life. The metal flowrate upstream of the baffles can be decreased by 6%, and the flow velocity on the upper sidewall and bottom wall decrease by 9% and 7%, respectively, compared with the base model. By using baffles, the minimum fatigue life of the refractory in the main trough increases by 15 tappings compared with the base model, so the period between the maintenance stops can be prolonged by about 2 days.