Cobalt sulfide composites have exhibited great potential in terms of microwave absorption, owing to their low price, relatively high capacitance, and excellent electrocatalytic activity. Thus, a novel core-shell like structure comprising cobalt sulfide@polypyrrole (CoS@PPy) composite was synthesized by a facile solvothermal synthesis method and in situ polymerization. When coated by the heterostructure polypyrrole aerogel, CoS@PPy composite exhibited excellent microwave absorption properties with an optimal reflection loss (R_L) of −41.8 dB at 6.96 GHz. Furthermore, the absorption bandwidth (R_L < −10 dB) of 5.4 GHz could be reached at a coating thickness of 2.05 mm, probably attributing to the synergistic effect of good impedance matching, interfacial polarization, dipole polarization, and conductivity loss. Moreover, this work proposed a loss mechanism mode which probably occurred in the CoS@PPy composites. It was demonstrated that the CoS@PPy composite is a promising material in the field of electromagnetic wave absorption.

As a typical two-dimensional material, MXene possesses excellent conductivity and tunable interlayer space, which makes it have an impressive development potential in the field of electromagnetic (EM) waves absorbing materials. In this work, we fabricated a sandwich structure CoS@Ti₃C₂T_x composite using a simple solvothermal process. The CoS nanoparticles are anchored on the Ti₃C₂T_x MXene sheets, forming a heterolayered structure. The results demonstrate that the CoS@Ti₃C₂T_x composites with the sandwich-like architecture showed excellent EM absorbing performance due to the synergistic effects of the conductivity loss, interface polarization, and dipole polarization. When the doping ratio was 40 wt %, the maximum reflection loss value of CoS@Ti₃C₂T_x was up to –59.2 dB at 14.6 GHz, and the corresponding effective absorption bandwidth (below –10 dB) reached 5.0 GHz when the thickness was only 2.0 mm. This work endows a new candidate for the design of MXene-based absorption materials with optimal performance.

A novel CoS@Fe₃O₄@rGO aerogel with a unique 3D porous heterostructure was prepared via the solvothermal method, in which cobalt sulfide (CoS) microspheres embedded with Fe₃O₄ nanoparticles were randomly scattered on reduced graphene oxide (rGO) flakes. The introduction of magnetic Fe₃O₄ nanoparticles and rGO regulated the impedance matching, and the excellent electromagnetic wave (EMW) absorption capability of the CoS@Fe₃O₄@rGO aerogel could be attributed to optimal dielectric loss and abundant conductive networks. The results demonstrated that the minimum reflection loss (RL) value of CoS@Fe₃O₄@rGO aerogel was −60.65 dB at a 2.5 mm coating thickness with an ultra-wide bandwidth of 6.36 GHz (10.24–16.6 GHz), as the filler loading was only 6 wt%. Such a lightweight CoS@Fe₃O₄@rGO aerogel with an outstanding absorbing intensity and an ultra-wide effective absorption bandwidth could become a potential EMW absorber.

The key step of camouflage effectiveness evaluation is how to combine the human visual physiological features, psychological features to select effectively evaluation indexes. Based on the predecessors’ camo comprehensive evaluation method, this paper chooses the suitable indexes combining with the image quality awareness, and optimizes those indexes combining with human subjective perception. Thus, it perfects the theory of index extraction.

This paper introduces the technical indicators related to the deformed disruptive pattern camouflage in China's national military standards, and discusses the expansion and supplement of the existing national military standard from the development of reconnaissance technology. It is recommended to increase the content of anti-military reconnaissance in the optical camouflage index; it is suggested that the speckle size shape technical index gives quantitative provisions based on the characteristic values such as area, perimeter and elongation; it is recommended to establish the relevant technical indicators of optical camouflage.