In this paper, we have investigated the deposition of thin films from natural carvacrol extract using dielectric barrier discharge (DBD) plasma polymerization, aiming at the inhibition of bacteria adhesion and proliferation. The films deposited on stainless steel samples have been characterized by scanning electron microscopy, infrared reflectance-absorbance spectroscopy, profilometry, and contact angle measurements. Films with thicknesses ranging from 1.5 μm to 3.5 μm presented a chemical structure similar to that of carvacrol. While the formation of biofilm was observed on untreated samples, the coating completely inhibited the adhesion of E. coli and reduced the adhesion of S. aureus biofilm in more than 90%.

Titanium dioxide has attracted a great deal of attention in the field of environmental purification due to its photocatalytic activity under ultraviolet light. Photocatalytic efficiency and the energy required to initiate the process remain the drawbacks that hinder the widespread adoption of the process. Consistently with this, it is proposed here the polymerization of hexamethyldisiloxane fragments simultaneously to TiO₂ sputtering for the production of thin films in low-pressure plasma. The effect of plasma excitation power on the molecular structure and chemical composition of the films was evaluated by infrared spectroscopy. Wettability and surface energy were assessed by a sessile drop technique, using deionized water and diiodomethane. The morphology and elemental composition of the films were determined using scanning electron microscopy and energy dispersive spectroscopy, respectively. The thickness and roughness of the resulting films were measured using profilometry. Organosilicon-to-silica films, with different properties, were deposited by combining both deposition processes. Titanium was detected from the structures fabricated by the hybrid method. It has been observed that the proportion of titanium and particles incorporated into silicon-based matrices depends on the plasma excitation power. In general, a decrease in film thickness with increasing power has been observed. The presence of Ti in the plasma atmosphere alters the plasma deposition mechanism, affecting film deposition rate, roughness, and wettability. An interpretation of the excitation power dependence on the plasma activation level and sputtering yield is proposed. The methodology developed here will encourage researchers to create TiO₂ films on a range of substrates for their prospective use as sensor electrodes, water and air purification systems, and biocompatible materials.

Eugenol (4-Allyl-2-methoxyphenol) is the main constituent of clove oil. In addition to being widely used as a condiment, it has been recognized as a powerful bactericide. Owing to that, Eugenol has been used in several applications including odontology and as a conservative for food products. Aiming at the development of natural bactericide coatings, in this work, using an atmospheric pressure plasma in a dielectric barrier discharge (DBD) reactor Eugenol was deposited on stainless steel substrate, with argon as a carrier gas. The discharge power supply was a transformer at 14.4 kV peak-to-peak voltage and 60 Hz frequency. Operating with a gas flow rate at 4 L/min, the active power was around 1.2 W. The maximum plasma electron temperature of the plasma with monomers was about 1.5 eV, estimated by visible emission spectroscopy using a local thermodynamic equilibrium approach. The study also comprehended the analysis of the film structure, aging, and thermal stability using infrared reflectance spectroscopy, and its thicknesses and roughness by profilometry. The thickness of the films was in the range of 1000 to 2400 nm with a roughness of up to 800 nm with good adhesion on the substrate. The FTIR result shows a stable coating with a chemical structure similar to that of the monomer. Aging analysis showed that the film does not degrade, even after exposing the film for 120 days in ambient air and for 1.0 h under a high thermal UV-lamp.