Fiber optic sensors have long been considered for use in structural health monitoring of components because of their small size, high accuracy, and their ability to perform spatially distributed strain measurements when embedded within a component or on its surface. The typical method for transferring strain from the component to the fiber is to use an epoxy, which may not survive extended exposure to high temperatures, thus necessitating a more elaborate technique to embed the fibers. This work represents a first step towards using additive manufacturing techniques to embed fiber optic sensors on stainless steel components for high-temperature strain monitoring, including quantification of the differential thermal strains that develop between the fiber and the steel substrate. Copper-coated optical fibers were embedded in nickel layers on top of a stainless steel substrate using an ultrasonic additive manufacturing technique. The embedded fibers showed minimal signal attenuation and clear compressive strain after embedding. Heating the embedded fibers in steps to temperatures of 300 °C–400 °C resulted in measured strains with values between the expected thermal strain in stainless steel and nickel. Finite element simulations confirm the measured strain values and show that the thermal strain depends on the thickness of the nickel layers deposited on top of the stainless steel substrate. While the fibers failed before reaching temperatures of 500 °C, it is suspected that these failures occurred due to a combination of (1) the lack of strain relief, (2) the high-temperature oxidation of the fiber’s copper coating, and (3) improper sizing of the machined channel in which the fiber is placed prior to embedding. If proper coating selection and sizing of the channel can prevent the failures observed in this work, the next step would be to monitor strain during mechanical loading at high temperatures.

This paper discusses the development, processing steps, and evaluation of a smart build-plate or baseplate tool for metal additive manufacturing technologies. This tool uses an embedded high-definition fiber optic sensing fiber to measure strain states from temperature and residual stress within the build-plate for monitoring purposes. Monitoring entails quality tracking for consistency along with identifying defect formation and growth, i.e., delamination or crack events near the build-plate surface. An aluminum alloy 6061 build-plate was manufactured using ultrasonic additive manufacturing due to the process’ low formation temperature and capability of embedding fiber optic sensing fiber without damage. Laser-powder bed fusion (L-PBF) was then used to print problematic geometries onto the build-plate using AlSi10Mg for evaluation purposes. The tool identified heat generation, delamination onset, and delamination growth of the printed L-PBF parts.