The rolling process of rings is a commonly used method for producing annular forgings. There are two primary types of this process: radial-axial rolling and radial rolling. This article presents the research results regarding the latter, in which obtaining a product with the assumed dimensions constitutes a major problem. In industrial practice, the process parameters are based on the experience of technologists and/or by trial and error. This is why the authors considered it justified to undertake the research aimed at determining the influence of the main process parameters, that is, preform temperature and tool speed, on the shape and dimensions of the cross-section, which determine the internal and external diameters of the rolled ring. The research was based on numerical simulations and experimental studies. The results obtained proved that the higher the feed speed of the main roll, the greater the change in the cross-sectional height during rolling, and the smaller the cross-sectional deformation (the so-called fishtail). Nevertheless, a higher preform temperature reduces the final height of the ring and reduces cross-section deformation. On the basis of the obtained test results, guidelines for the process design were postulated, considering the influence of temperature and speed parameters on the final dimensions of the forging and the dimensions of the preform.

This article provides a detailed review of the types of magnesium wheels available in the industry and the current methods of the wheels’ production. The past several years have seen a significant development of magnesium-based lightweight alloys employed as a structural material for modern light vehicles. Magnesium alloys are characterized by their low density while maintaining good mechanical properties. The use of these alloys in the industry enables vehicles’ weight reduction while increasing their technical parameters. The first part of the article presents the unique properties of magnesium alloys that determine the application of this material for lightweight vehicle wheels. The advantages of using magnesium wheels over aluminum wheels are also presented. Next, a classification of the types of magnesium wheels was made in regard to their construction, applications, and manufacturing methods. At present, magnesium wheels by construction can be classified according to their geometry as single parts or assembled parts. In reference to geometry, wheels can have different shapes: classic, multi-spoke, with holes, or with frames. Depending on the geometry used, magnesium wheels can have different parameters, such as their mounting hole spacing, wheel diameters, or rim width. Considering the applications in various industries, main distinctions can be made between magnesium wheels for automobiles, motorcycles, bicycles, and wheelchairs. Magnesium wheels can also be categorized in regards to the manufacturing methods: casting, machining, forging, and hybrid manufacturing. The second part of the article focuses on the analysis of magnesium alloy wheel-manufacturing technologies used in the industry and developed by research centers. This article discusses these manufacturing technologies in detail and indicates prospective directions for further development.

This article presents the analysis of the deformability, structure and properties of the AZ61 cast magnesium alloy on the example of a new forging process of aircraft mount forgings. It was assumed that their production process would be based on drop forging on a die hammer. Two geometries of preforms, differing in forging degree, were used as the billet for the forging process. It was assumed that using a cast, unformed preform positively affects the deformability of hard-deformable magnesium alloys and flow kinematics during their forging and reduces the number of operations necessary to obtain the correct product. Numerical analysis of the proposed new technology was carried out using DEFORM 3D v.11, a commercial program dedicated to analyzing metal forming processes. The simulations were performed in the conditions of spatial strain, considering the full thermomechanical analysis. The obtained results of numerical tests confirmed the possibility of forming the forgings of aviation mounts from the AZ61 cast magnesium alloy with the proposed technology. They also allowed us to obtain information about the kinematics of the material flow during forming and process parameters, such as strain intensity distribution, temperatures, Cockcroft–Latham criterion and forming energy. The proposed forging process on a die hammer was verified in industrial conditions. The manufactured forgings of aircraft mounts made of AZ61 magnesium alloy were subjected to qualitative tests in terms of their structure, conductivity and mechanical properties.

Hot ring rolling is a method of forming ring products with large diameters in relation to the cross-sectional dimensions. This process is a complex incremental metal forming process. It is characterized by high dynamics and continuous change of hape of the rolled ring. Important process...

Magnesium alloys are highly strain rate sensitive and exhibit good workability in a narrow forging temperature range. Consequently, parts made of these materials are usually forged with low-speed hydraulic presses, using specially designed tool heating systems in order to ensure near-isothermal conditions. This study investigates whether popular magnesium alloys such as Mg-Al-Zn can be forged in forging machines equipped with high-speed forming tools. Experimental upset forging tests on AZ31B, AZ61A and AZ80A specimens were conducted, using a screw press with a ram speed of 0.5 m/s and a die forging hammer with a ram speed at stroke of about 5 m/s. Test specimens were preheated to 350 °C, 410 °C and 450 °C. After the upset forging process, they were air- or water-cooled and then examined for their workability, hardness and grain size. To validate the results, a forging process for a producing handle was designed and modelled by the finite element method. Distributions of strain, temperature and fracture criterion were analysed, and energy and force parameters of the forging process were calculated. After that, experimental tests were performed on AZ31B and AZ61A specimens in order to determine mechanical properties of forged parts and examine their micro- and macrostructure. Results have demonstrated that AZ80A is not suitable for forging with either the screw press or the die forging hammer, that AZ61A can be press- and hammer-forged but to a limited extent, and that AZ31B can be subjected to forging in both forging machines analysed in the study.

The article discusses the influence of heat treatment and metal forming parameters on formability and the structure of the AZ91 cast magnesium alloy. The aim of the article is to determine the optimal parameters of homogenization and plastic deformation of sand castings made of the AZ91 alloy in...