The study presents the results of investigations of modeling the usable properties of implant surfaces made of Ti6Al7Nb alloy, using the example of a dynamic hip screw (DHS) applied in surgical treatment of intertrochanteric femoral neck fractures. Numerical simulation has been performed for the model load of femoral fixation with DHS screw. The load simulation results provided the basis to select mechanical properties of the fixator elements and to define those fixation areas which are mostly susceptible to development of corrosion. The surfaces of Ti6Al7Nb alloy were ground, vibro-abrasive machined, mechanically polished, sandblasted, anode oxidized at different voltage values and steam sterilized. Results of surface topography evaluation, resistance to pitting and crevice corrosion as well as degradation kinetics of the outer layer were presented. Usability of the formed passive layer in clinical applications was evaluated through wear and corrosion tests of the femoral fixation model. The test results proved usefulness of the proposed surface modification methods for clinical application of different size and shape implants

The study discusses the methods of surface modification methods for AISAI 316 L steel and Ti6Al4V ELI titanium alloy, dedicated to complex design implants used in bone surgery. Results of structural tests have been presented along with those evaluating the physicochemical properties of the formed surface layers. Clinical feasibility of the surface layers has also been evaluated.The developed surface modification methods improved the resistance to pitting, crevice and stress corrosion and ensured better biocompatibility. Moreover, the layers formed are marked by plasticity. Results of the tests performed show applicability of the evaluated methods of surface modification in complex shape implants for the clinical use.

The main goal of carried out tests were the impact of physicochemical properties of surface layers on the course of processes taking place on the surface of implants made of metallic biomaterials used in the bone system. As a precursor of ZnO, diethylzinc (DEZ) has been used, which reacted with water enabling the deposition of thin films. The chamber temperature was as follows—T = 200°–300 °C. The number of cycles was 500, 1000, and 1500. In the first stage, pitting corrosion test was carried out. Corrosion resistance has been tested under conditions simulating tissue environment. Moreover, the created layers were tested using electrochemical impedance spectroscopy (EIS). The conducted electrochemical tests showed the beneficial effect of the ZnO layer on the substrate made of 316 LVM steel, as evidenced by the obtained parameters describing the corrosion resistance. Furthermore, tests were performed on mechanical properties (scratch test), surface morphology (SEM and AFM method), and physical properties (wettability and thickness layers) for samples with different surface treatments. The investigations of the surface morphology of the applied ZnO layer using the ALD method showed a tendency to inherit the substrate independently of the used application parameters. On the other hand, the tests of adhesion to the substrate showed that the number of cycles of the application process has a fundamental impact on the adhesion of the applied layer to the substrate. Summarizing tests have clearly shown that the number of cycles and temperature in the case of the ZnO coating is significant and positively influences the increase of electrochemical, mechanical, and physical properties of layers.