A series of new poly(ethylene oxide) (PEO)-based copolyimides varying in hard segment structure are reported in this work as CO₂ selective separation membranes. Their structural diversity was achieved by using different aromatic dianhydrides (4,4′-oxydiphthalic anhydride (ODPA), 4,4’-(hexafluoroisopropylidene)diphthalic anhydride (6FDA)) and diamines (4,4′-oxydianiline (ODA), 4,4′-(4,4′-isopropylidene-diphenyl-1,1′- diyldioxy)dianiline (IPrDA), 2,3,5,6-tetramethyl-1,4-phenylenediamine (4MPD)), while keeping the content of PEO (2000 g/mol) constant (around 50%). To get a better insight into the effects of hard segment structure on gas transport properties, a series of aromatic polyimides with the same chemistry was also studied. Both series of polymers were characterized by ¹HNMR, FTIR, WAXD, DSC, TGA, and AFM. Permeabilities for pure He, O₂, N₂, and CO₂ were determined at 6 bar and at 30 °C, and for CO₂ for pressures ranging from 1 to 10 bar. The results show that OPDA-ODA-PEO is the most permeable copolyimide, with CO₂ permeability of 52 Barrer and CO₂/N₂ selectivity of 63, in contrast to its fully aromatic analogue, which was the least permeable among polyimides. 6FDA-4MPD-PEO ranks second, with a two times lower CO₂ permeability and slightly lower selectivity, although 6FDA-4MPD was over 900 times more permeable than OPDA-ODA. As an explanation, partial filling of hard domain free voids by PEO segments and imperfect phase separation were proposed.

In this work, we studied the stability of matrices with temperature-dependent solubility and their interactions with water at physiological temperature for their application in cell culture in vitro. Gradient copolymers of 2-isopropyl- with 2-n-propyl-2-oxazoline (P(iPrOx-nPrOx)) were used to prepare the matrices. The comonomer ratio during polymerization was chosen such that the cloud point temperature (T_CP) of the copolymer was below 37 °C while the glass transition (T_g) was above 37 °C. The role of the support for matrices in the context of their stability in aqueous solution was examined. Therefore, matrices in the form of both self-supported bulk polymer materials (fibrillar mats and molds) and polymer films supported on the silica slides were examined. All of the matrices remained undissolved when incubated in water at a temperature above T_CP. For the self-supported mats and molds, we observed the loss of shape stability, but, in the case of films supported on silica slides, only slight changes in morphology were observed. For a more in-depth investigation of the origin of the shape deformation of self-supported matrices, we analyzed the wettability, thickness, and water uptake of films on silica support because the matrices remained undeformed under these conditions. It was found that, above the T_CP of P(iPrOx-nPrOx), the wettability of the films decreased, but at the same time the films absorbed water and swelled. We examined how this specific behavior of the supported films influenced the culture of fibroblasts. The temperature-dependent solubility of the matrices and the possibility of noninvasive cell separation were also examined.

Poly(L-lactide) is capable of self-assembly into a nematic mesophase under the influence of temperature and mechanical stresses. Therefore, subsequent poly(L-lactide) films were obtained and characterized, showing nematic liquid crystal properties both before and after degradation. Herein, we present that, by introducing β-cyclodextrin into the polymer matrix, it is possible to obtain a chiral nematic mesophase during pressing, regardless of temperature and time. The obtained poly(L-lactide) films exhibiting liquid crystal properties were subjected to degradation tests and the influence of degradation on these properties was determined. Thermotropic phase behavior was investigated using polarized optical microscopy, X-ray diffraction, and differential scanning calorimetry. The degradation process demonstrated an influence on the liquid crystal properties of pressed polymer films. The colored planar texture of the chiral nematic mesophase, which was not observed prior to degradation in films without the addition of β-cyclodextrin, appeared after incubation in water as a result of the entrapment of degradation products in the polymer matrix. These unusual tailor-made properties, obtained in liquid crystals in (bio)degradable polymers using a simple method, demonstrate the potential for advanced photonic applications.

The optical properties, electronic structure and morphology of thin films of the polymer donor PTB7-Th blended with either the fullerene acceptor PC70BM or the non-fullerene acceptor ZY-4Cl were systematically investigated to evaluate their annealing-induced evolution. Thin films were characterized using UV–Vis–NIR absorption spectroscopy, spectroscopic ellipsometry, ATR-FTIR spectroscopy, atomic force microscopy (AFM), and nano-IR analysis. In situ stepwise thermal annealing revealed distinct changes in absorption edge parameters, indicating thermally induced modifications in the electronic structure of the blend films. Ellipsometric analysis showed that elevated temperatures significantly affect the refractive index and extinction coefficient spectra. AFM measurements demonstrated markedly different surface morphology evolution for the two blend systems, with pronounced needle-shaped crystallites formation observed in PTB7-Th:ZY-4Cl films after annealing at 100 °C. Nano-IR characterization identified these crystallites as predominantly PTB7-Th, indicating phase separation driven by thermal treatment. The combined optical and structural results reveal distinct annealing-induced changes in the blend. Finally, BHJ solar cells, based on PTB7-Th:PC70BM and PTB7-Th:ZY-4Cl active layers, were fabricated, and their photovoltaic response was demonstrated.