In this study, chitosan (CS) grafted by glycidyltrimethylammonium chloride (GTMAC) to form GTMAC-CS was synthesized, chemically identified, and rheologically characterized. The Maxwell Model can be applied to closely simulate the dynamic rheological performance of the chitosan and the GTMAC-CS solutions, revealing a single relaxation time pertains to both systems. The crossover point of G′ and Gʺ shifted toward lower frequencies as the CS concentration increased but remained almost constant frequencies as the GTMAC-CS concentration increased, indicating the solubility of GTMAC-CS in water is good enough to diminish influence from the interaction among polymer chains so as to ensure the relaxation time is independent of the concentration. A frequency–concentration superposition master curve of the CS and GTMAC-CS solutions was subsequently proposed and well fitted with the experimental results. Finally, the sol-gel transition of CS is 8.5 weight % (wt %), while that of GTMAC-CS is 20 wt %, reconfirming the excellent water solubility of the latter.

A UV-curable, flame-retardant monomer, DAPP (bis[di-acryloyloxyethyl]-p-tert-butyl-phenyl-phosphate), was synthesized based on BPDCP (4-tert-butylphenyl-dichloro phosphate) and HEA (2-hydroxy ethyl acrylate). DAPP was blended with regular bisphenol A epoxy acrylate (BAEA) in various ratios to yield various phosphorus contents. The TGA-IR (thermogravimetric analyzer interface with an infrared spectrometer) results demonstrate that compounding 30 mol % DAPP with BAEA significantly reduced the amount of released CO gas. In contrast, the peak intensity of CO₂ is independent of phosphorus content. The limiting oxygen index (LOI), reaching the saturated value of 26, and the heat release rate (HRR) measured using a cone-calorimeter, 156.43 KW/m², confirm the saturation point when 30 mol % DAPP was compounded into BAEA. A study of the kinetics of pyrolysis reveals that E_a decreases as the phosphorus content increases. Both the TGA-IR and pyrolysis results reveal that the phosphorus compound DAPP is easily decomposed during the initial stage of burning to form an insulating layer, which inhibits further burning of the resin and the consequent release of other flammable gases.

PCL-based biodegradable shape-memory polymers (SMPs) are limited in strength, which restricts their practical applications. In this study, a series of novel SMPs, composed of poly(ethylene terephthalate) (PET), poly(ethylene naphthalate) (PEN), and poly(ε-caprolactone) (PCL), were synthesized and cross-linked using planar (benzene-1,3,5-tricarboxylic acid, BTC) or non-planar (glycerol, GC) cross-linkers via the one-pot method. The influence of different kinds of cross-linkers and hard segments of copolyesters on the thermal properties, crystallization behavior, mechanical properties, shape-memory performance, and degradability was investigated by FT-IR, ¹H-NMR, DSC, DMA, TGA, XRD, tensile test, intrinsic viscosity measurement, and in vitro enzymatic degradation test. The results indicate that the tensile strength of the copolyester can be significantly improved from 27.8 to 53.2 MPa by partially replacing PET with PEN while maintaining its shape-memory characteristics. Moreover, a small amount of cross-linking modification leads to higher temperature sensitivity, improved shape recovery rate at third round (R_r(3) = 99.1%), and biodegradability in the cross-linked PET/PEN/PCL shape-memory polymers. By changing the crystallization morphology and cross-linking forms of the material, we have developed a shape-memory polymer with both high strength and a high shape recovery rate, which provides a new strategy for the development of shape-memory materials.