This paper discusses the effect of different heat treatment procedures on the microstructural characteristics, damping capacities, and mechanical properties of CuAlNi shape memory alloys (SMA). The investigation was performed on samples in the as-cast state and heat treated states (solution annealing at 885 °C/60′/H₂O and after tempering at 300 °C/60′/H₂O). The microstructure of the samples was examined by light microscopy (LM) and scanning electron microscopy (SEM) equipped with a device for energy dispersive spectrometry (EDS) analysis. Light and scanning electron microscopy showed martensitic microstructure in all investigated samples. However, the changes in microstructure due to heat treatment by the presence of two types of martensite phases (β_1′ and γ_1′) influenced alloy damping and mechanical properties by enhancing alloy damping characteristics. Heat treatment procedure reduced the alloys’ mechanical properties and increased hardness of the alloy. Fractographic analysis of the alloy showed a transgranular type of fracture in samples after casting. After solution annealing, two types of fracture mechanisms can be noticed, transgranular and intergranular, while in tempered samples, mostly an intergranular type of fracture exists.

Microstructural and cavitation erosion testing was carried out on Cu-12.8Al-4.1Ni (wt. %) shape memory alloy (SMA) samples produced by continuous casting followed by heat treatment consisting of solution annealing at 885 °C for 60 min and, later, water quenching. Cavitation resistance testing was applied using a standard ultrasonic vibratory cavitation set up with stationary specimen. Surface changes during the cavitation were monitored by metallographic analysis using an optical microscope (OM), atomic force microscope (AFM), and scanning electron microscope (SEM) as well as by weight measurements. The results revealed a martensite microstructure after both casting and quenching. Microhardness value was higher after water quenching than in the as-cast state. After 420 min of cavitation exposure, a negligible mass loss was noticed for both samples. Based on the obtained results, both samples showed excellent cavitation resistance. Mass loss and morphological analysis of the formed pits indicated better cavitation resistance for the as-cast state (L).

This paper presents the results of thermal and microstructural analysis of Cu-Al-Ni shape memory alloy before and after heat treatment. After casting, a bar of Cu-12.8 Al-4.1 Ni (wt.%) alloy, obtained by the vertical continuous casting technique, was subjected to a certain heat treatment procedure. Solution annealing was performed at 850 °C for 60 min, followed by water quenching. Tempering was then performed at four different temperatures (150 °C, 200 °C, 250 °C and 300 °C). The microstructural results were obtained by optical and scanning electron microscopy. Thermodynamic calculation of ternary Cu-Al-Ni system under equilibrium was performed using Thermo-Calc 5 software. Phase transformation temperatures were determined by differential scanning calorimetry (DSC). The DSC results show the highest values of transformation temperatures in as-cast state. After solution annealing and tempering, the transformation temperatures show lower values with exceptional stability of Ms temperature (martensite start temperature).