The integration of 3D printed sensors into hosting structures has become a growing area of research due to simplified assembly procedures, reduced system complexity, and lower fabrication cost. Embedding 3D printed sensors into structures or bonding the sensors on surfaces are the two techniques for the integration of sensors. This review extensively discusses the fabrication of sensors through different additive manufacturing techniques. Various additive manufacturing techniques dedicated to manufacture sensors as well as their integration techniques during the manufacturing process will be discussed. This review will also discuss the basic sensing mechanisms of integrated sensors and their applications. It has been proven that integrating 3D printed sensors into infrastructures can open new possibilities for research and development in additive manufacturing and sensor materials for smart goods and the Internet of Things.

This article outlines the current state-of-the-art binder jetting (BJT) additive manufacturing of functional ceramics. The impact of printing parameters, heat treatment processing, and testing conditions on the observed performance of these ceramics is discussed. Additionally, this article discusses the impact of physical properties such as density and mechanical strength on the overall performance of these functional ceramics. Although printing parameters and initial feedstock are crucial for the printability of the desired parts, other factors play an important role in the performance of the ceramic. Thermal post-processing is crucial to achieve optimized functional properties, while the testing orientation is key to obtaining the maximum output from the part. Finally, future research directions for this field are also discussed.

The growing demand for wearable devices, soft robotics, and tissue engineering in recent years has led to an increased effort in the field of soft materials. With the advent of personalized devices, the one-shape-fits-all manufacturing methods may soon no longer be the standard for the rapidly increasing market of soft devices. Recent findings have pushed technology and materials in the area of additive manufacturing (AM) as an alternative fabrication method for soft functional devices, taking geometrical designs and functionality to greater heights. For this reason, this review aims to highlights recent development and advances in AM processable soft materials with self-healing, shape memory, electronic, chromic or any combination of these functional properties. Furthermore, the influence of AM on the mechanical and physical properties on the functionality of these materials is expanded upon. Additionally, advances in soft devices in the fields of soft robotics, biomaterials, sensors, energy harvesters, and optoelectronics are discussed. Lastly, current challenges in AM for soft functional materials and future trends are discussed.

Thermoplastic materials such as PA12 and PA6 have been extensively employed in Selective Laser Sintering (SLS) 3D printing applications due to their printability, processability, and crystalline structure. However, thermoplastic-based materials lack polymer inter-chain bonding, resulting in inferior mechanical and thermal properties and relatively low fatigue behavior. Therefore, 3D printing of high-performance crosslinked thermosets using SLS technology is paramount to pursue as an alternative to thermoplastics. In this work, a thermoset resin was successfully 3D printed using SLS, and its thermal stability of printed parts after a multi-step post-curing process was investigated. Dimensionally stable and high glass transition temperature (T_g: ~300 °C) thermoset parts were fabricated using SLS. The polymer crosslinking mechanism during the printing and curing process was investigated through FTIR spectra, while the mechanical stability of the SLS 3D-printed thermoset was characterized through compression tests. It is found that 100% crosslinked thermoset can be 3D printed with 900% higher compressive strength than printed green parts.

Purpose: Shape memory polymer (SMP) is capable of recovering its original shape from a high degree of deformation by applying an external stimulus such as thermal energy. This research presents an integration of two commercial SMP materials (DiAPLEX and Tecoflex) and a material extrusion (ME) printer to fabricate SMP parts and specimens. The material properties such as Young’s modulus of the specimens was examined as a process output. Furthermore, stress-strain curve, strain recovery, instant shape-fixity ratio, long-term shape-fixity ratio and recovery ratio of SMP specimens during a thermo-mechanical cycle were investigated. Design/methodology/approach: The ME fabrication settings for the SMP specimens were defined by implementing a design of experiments with temperature, velocity and layer height as process variables. Findings: It was found, according to main effect and iteration plots, that fabrication parameters have an impact on Young’s modulus and exist minimum iteration among variables. In addition, Young’s modulus variation of DiAPLEX and Tecoflex specimens was mostly caused by velocity and layer height parameters, respectively. Moreover, results showed that SMP specimens were able to recover high levels of deformation. Originality/value: This paper is a reference for process control and for rheological properties of SMP parts produced by ME fabrication process.

This research presents a simple method to additively manufacture Cone 5 porcelain clay ceramics by using the direct ink-write (DIW) printing technique. DIW has allowed the application of extruding highly viscous ceramic materials with relatively high-quality and good mechanical properties, which additionally allows a freedom of design and the capability of manufacturing complex geometrical shapes. Clay particles were mixed with deionized (DI) water at different ratios, where the most suitable composition for 3D printing was observed at a 1:5 w/c ratio (16.2 wt.%. of DI water). Differential geometrical designs were printed to demonstrate the printing capabilities of the paste. In addition, a clay structure was fabricated with an embedded wireless temperature and relative humidity (RH) sensor during the 3D printing process. The embedded sensor read up to 65% RH and temperatures of up to 85 °F from a maximum distance of 141.7 m. The structural integrity of the selected 3D printed geometries was confirmed through the compressive strength of fired and non-fired clay samples, with strengths of 70 MPa and 90 MPa, respectively. This research demonstrates the feasibility of using the DIW printing of porcelain clay with embedded sensors, with fully functional temperature- and humidity-sensing capabilities.