By anodization and thermal oxidation at 600 °C, an oxide layer on Ti with excellent corrosion resistance in strong acid solutions was prepared. The structural properties of TiO₂ films before and after thermal oxidation were investigated with methods of Scanning electron microscope (SEM), X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD). The electrochemical characterization was recorded via electrochemical impedance spectroscopy, potentiodynamic polarization and Mott–Schottky methods. XRD results show that a duplex rutile/anatase structure formed after oxidation, and the amount of anatase phase increased as the treatment time was prolonged from 3 to 9 h. XPS analysis indicates that as the thermal oxidation time increased, more Ti vacancies were present in the titanium oxide films, with decreased donor concentration. Longer thermal oxidation promoted the formation of hydroxides of titanium on the surface, which is helpful to improve the passive ability of the film. The anodized and thermally oxidized Ti samples showed relatively high corrosion resistance in 4 M HCl and 4 M H₂SO₄ solutions at 100 ± 5 °C. The passive current density values of the thermally oxidized samples were five orders of magnitude under the testing condition compared with that of the anodized sample. With the oxidation time prolonged, the passive current density decreased further to some extent.

In this work, a slippery lubricant-infused surface (LIS) was prepared by simple one-step mixing of polydimethylsiloxane (PDMS) resin and dimethyl silicone oil (PMX-200) directly. Silicone oil showed good compatibility with PDMS resin, and the added amount of silicone oil had no significant effect on the surface morphology of LIS. According to the results of surface observations, once the silicone oil film anchored on the LIS was removed, the silicone oil inside the PDMS polymer automatically diffused to the surface and formed a new silicone oil film again in a short time. Furthermore, with the increase of silicone oil content, the oil self-replenishment speed and amount of the LIS were enhanced, which also promoted a decrease of the surface water sliding angle and the improvement of the lubrication ability of the LIS. In the icing/deicing cycle tests, the slippery LIS still maintained very low ice adhesion strength after 24 cycles, showing excellent anti-icing performance.

Epoxy coating is a commonly used anticorrosive coating on metal surfaces. Pseudomonas aeruginosa has been reported to be able to accelerate the corrosion of metal materials, but its effect on the corrosion resistance of epoxy coatings is rarely reported. In this work, the accelerated deterioration of epoxy coating on carbon steel caused by marine Pseudomonas aeruginosa was investigated. The immersion tests of epoxy coatings in the sterile and P. aeruginosa-inoculated culture media with 100%, 10%, and 0% nutrients were performed. When the nutrient concentration was reduced, the number of P. aeruginosa cells attached to the coating surface was improved, and the coatings suffered more degradation under starvation conditions. The results of electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization measurements showed that the presence of P. aeruginosa promoted the degradation of epoxy coating, and the coating had lower low frequency impedance modulus and higher corrosion current density in the inoculated medium with starvation conditions. The results of Fourier transform infrared spectroscopy (FTIR) indicated that the peak intensities of C-O-C and C-O groups of coatings decreased as nutrient concentration dropped in the inoculated medium. It indicated that P. aeruginosa accelerated the degradation of epoxy coatings through destroying the C-O-C and C-O groups.