Silica nanoparticles (SiO₂ NPs) synthesized by the Stober method were used as drug delivery vehicles. Doxorubicin hydrochloride (DOX·HCl) is a chemo-drug absorbed onto the SiO₂ NPs surfaces. The DOX·HCl loading onto and release from the SiO₂ NPs was monitored via UV-VIS and fluorescence spectra. Alternatively, the zeta potential was also used to monitor and evaluate the DOX·HCl loading process. The results showed that nearly 98% of DOX·HCl was effectively loaded onto the SiO₂ NPs’ surfaces by electrostatic interaction. The pH-dependence of the process wherein DOX·HCl release out of DOX·HCl-SiO₂ NPs was investigated as well. For comparison, both the free DOX·HCl molecules and DOX·HCl-SiO₂ NPs were used as the labels for cultured cancer cells. Confocal laser scanning microscopy images showed that the DOX·HCl-SiO₂ NPs were better delivered to cancer cells which are more acidic than healthy cells. We propose that engineered DOX·HCl-SiO₂ systems are good candidates for drug delivery and clinical applications.

In this work, the preparation of magneto-plasmonic granular nanostructures and their evaluation as efficient substrates for magnetically assisted surface enhanced Raman spectroscopy (SERS) sensing are discussed. These nanostructures consist of star-shaped gold Au shell grown on iron oxide Fe_3-xO₄ multicores. They were prepared by seed-mediated growth of anisotropic, in shape gold nanosatellites attached to the surface of polyol-made iron oxide polycrystals. In practice, the 180 nm-sized spherical iron oxide particles were functionalized by (3-aminopropyl) triethoxysilane (APTES) to become positively charged and to interact, in solution, with negatively charged 2 nm-sized Au single crystals, leading to nanohybrids. These hybrids acted subsequently as nucleation platforms for the growth of a branched gold shell, when they were contacted to a fresh HAuCl₄ gold salt aqueous solution, in the presence of hydroquinone, a reducing agent, for an optimized nominal weight ratio between both the starting hybrids and the gold salt. As expected, the resulting nanocomposites exhibit a high saturation magnetization at room temperature and a rough enough plasmonic surface, making them easily attracted by a lab. magnet, while exhibiting a great number of SERS hot spots. Preliminary SERS detection assays were successfully performed on diluted aqueous thiram solution (10⁻⁸ M), using these engineered substrates, highlighting their capability to be used as chemical trace sensors.

The formation of silver nanopetal-Fe₃O₄ poly-nanocrystals assemblies and the use of the resulting hetero-nanostructures as active substrates for Surface Enhanced Raman Spectroscopy (SERS) application are here reported. In practice, about 180 nm sized polyol-made Fe₃O₄ spheres, constituted by 10 nm sized crystals, were functionalized by (3-aminopropyl)triethoxysilane (APTES) to become positively charged, which can then electrostatically interact with negatively charged silver seeds. Silver petals were formed by seed-mediated growth in presence of Ag⁺ cations and self-assembly, using L-ascorbic acid (L-AA) and polyvinyl pyrrolidone (PVP) as mid-reducing and stabilizing agents, respectively. The resulting plasmonic structure provides a rough surface with plenty of hot spots able to locally enhance significantly any applied electrical field. Additionally, they exhibited a high enough saturation magnetization with M_s = 9.7 emu g⁻¹ to be reversibly collected by an external magnetic field, which shortened the detection time. The plasmonic property makes the engineered Fe₃O₄-Ag architectures particularly valuable for magnetically assisted ultra-sensitive SERS sensing. This was unambiguously established through the successful detection, in water, of traces, (down to 10⁻¹⁰ M) of Rhodamine 6G (R6G), at room temperature.