Post-mortem characterisation is a pivotal tool to trace back to the origin of structural failures in modern engineering analyses. This work compared both the crack propagation and rupture roughness profiles based on areal parameters for total fracture area. Notched and smooth samples made of weather-resistant structural steel (10HNAP), popular S355J2 structural steel and aluminium alloy AW-2017A under bending, torsion and combined bending–torsion were investigated. After the fatigue tests, fatigue fractures were measured with an optical profilometer, and the relevant surface parameters were critically compared. The results showed a great impact of the loading scenario on both the local profiles and total fracture areas. Both approaches (local and total fracture zones) for specimens with different geometries were investigated. For all specimens, measured texture parameters decreased in the following order: total area, rupture area and propagation area.

The study presented herein concerns the mechanical properties of two common polymers for potential biomedical applications, PLA and PETG, processed through fused filament fabrication (FFF)—Material Extrusion (ME). For the uniaxial tension tests carried out, two printing orientations—XY (Horizontal, H) and YZ (Vertical, V)—were considered according to the general principles for part positioning, coordinates, and orientation typically used in additive manufacturing (AM). In addition, six specimens were tested for each printing orientation and material, providing insights into mechanical properties such as Tensile Strength, Young’s Modulus, and Ultimate Strain, suggesting the materials’ potential for biomedical applications. The experimental results were then compared with correspondent mechanical properties obtained from the literature for other polymers like ASA, PC, PP, ULTEM 9085, Copolyester, and Nylon. Thereafter, fatigue resistance curves (S-N curves) for PLA and PETG, printed along 45°, were determined at room temperature for a load ratio, R, of 0.2. Scanning electron microscope observations revealed fibre arrangements, compression/adhesion between layers, and fracture zones, shedding light on the failure mechanisms involved in the fatigue crack propagation of such materials and giving design reference values for future applications. In addition, fractographic analyses of the fatigue fracture surfaces were carried out, as well as X-ray Computed Tomography (XCT) and Thermogravimetric (TGA)/Differential Scanning Calorimetric (DSC) tests.

In this research, a novel approach of the fatigue crack growth rate description has been proposed. Based on theoretical and experimental approach, the mean stress effect expressed by R-ratio is present in classical da/dN–Δ K diagram. According to energy approach – based on the irrevocably dissipated energy accumulated in material (hysteresis loop) during fatigue process – the mean stress effect can be minimalized. Experimental validation of the proposed model was performed using results of fatigue crack propagation data for S355 and 41Cr4 steels in terms of strain energy density parameter Δ S or cyclic J-integral range –Δ J. In contrast to the force approach based on K_max (or Δ K), the energy parameters Δ S or Δ J represent unambiguously the fatigue crack propagation rate, without influence of mean stress effect – R-ratio. However, in near threshold range of kinetic fatigue fracture diagram, the energy parameter displays a slight dispersion of the experimental data. According to the crack closure theory and its U-Elber parameter, the dispersion of experimental data is decreased. Therefore, the crack closure effects have a high significance in energy model – similar to the ‘force approach’ based on Δ K concept.