Persistent wound infections have been a therapeutic challenge for a long time. Current treatment approaches are mostly based on the delivery of antibiotics, but these are not effective for all infections. Here, we report the development of a sensitive pH-responsive hydrogel that can provide controlled, pH-triggered release of silver nanoparticles (AgNPs). This delivery system was designed to sense the environmental pH and trigger the release of AgNPs when the pH changes from acidic to alkaline, as occurs due to the presence of pathogenic bacteria in the wound. Our results show that the prepared hydrogel restricts the release of AgNPs at acidic pH (pH = 4) but substantially amplifies it at alkaline pH (pH = 7.4 and pH = 10). This indicates the potential use of the hydrogel for the on-demand release of Ag+ depending on the environmental pH. In vitro antibacterial studies demonstrated effective elimination of both Gram-negative and positive bacteria. Additionally, the effective antibacterial dose of Ag+ showed no toxicity towards mammalian skin cells. Collectively, this pH-responsive hydrogel presents potential as a promising new material for the treatment of infected wounds.

Polysorbate-80 (PS-80) is a common surfactant used in biologics formulations. However, the tendency of oxidation to PS-80 when exposed to stainless steel surfaces brings various challenges during manufacturing processes, such as inconsistent shelf-life of PS-80 solutions, which can further impact the biologics and vaccines production. In this work, the root causes of PS-80 oxidation when in contact with stainless steel conditions were thoroughly investigated through the use of various complementary analytical techniques including U/HPLC-CAD, LC-MS, ICP-MS, peroxide assay, and EPR spectroscopy. The analytical tool kit used in this work successfully revealed a PS-80 degradation mechanism from the perspective of PS-80 content, PS-80 profile, iron content, peroxide production, and radical species. The combined datasets reveal that PS-80 oxidative degradation occurs in the presence of histidine and iron in addition to being combined with the hydroperoxides in PS-80 material. The oxidative pathway and potential degradants were identified by LC-MS. The PS-80 profile based on the U/HPLC-CAD assay provided an effective way to identify early-signs of PS-80 degradation. The results from a peroxide assay observed increased hydroperoxide along with PS-80 degradation. EPR spectra confirmed the presence of histidine-related radicals during PS-80 oxidation identifying how histidine is involved in the oxidation. All assays and findings introduced in this work will provide insight into how PS-80 oxidative degradation can be avoided, controlled, or detected. It will also provide valuable evaluations on techniques that can be used to identify PS-80 degradation related events that occur during the manufacturing process.