This research endeavor aimed to develop thin film blends of polypyrrole (PPy) and poly (styrene-isoprene-styrene) (SIS) with MoO₃ as a nanofiller for improved mechanical and electrical properties to widen its scope in the field of mechatronics. This study reports blends of polypyrrole (PPy) and poly (styrene-isoprene-styrene) (SIS) tri-block copolymer showing improved mechanical and electrical attributes while employing MoO₃ nanobelts as nanofillers that additionally improves the abovementioned properties in the ensuing nanocomposites. The synthesis of PPy/SIS blends and MoO₃/PPy/SIS nanocomposites was well corroborated with XRD, SEM, FTIR, and EDS analysis. Successful blending of PPy was yielded up to 15 w/w% PPy in SIS, as beyond this self-agglomeration of PPy was observed. The results showed a remarkable increase in the conductivity of insulating SIS copolymer from 1.5 × 10^−6.1 to 0.343 Scm⁻¹ and tensile strength up to 8.5 MPa with the 15 w/w% PPy/SIS blend. A further enhancement of the properties was recorded by embedding MoO₃ nanobelts with varying concentrations of the nanofillers into 15 w/w% PPy/SIS blends. The mechanical strength of the polymeric nanocomposites was enhanced up to 11.4 MPa with an increase in conductivity up to 1.51 Scm⁻¹ for 3 w/w% MoO₃/PPy-SIS blends. The resultant product exhibited good potential for electro-mechanical dual applications.

Carbon nanorods have been synthesized from acetylene and steam using europium oxide nanorods as a template. The resulting carbon exhibits a high conductivity of 4.66 × 10⁵ S/m and a surface area of 1226 m²/g. The Eu₂O₃ was partially or completely washed from the carbon, creating hollow nanorods. Hybrid supercapacitors were fabricated where the Eu₂O₃ contributes a redox pseudocapacitance. A gravimetric capacitance of 501.2 F/g for the hybrid cell and 202 F/g for the carbon-only cell was measured at 1 A/g using 1 M lithium bis(trifluoromethanesulfonyl)imide (LiTFSI) in propylene carbonate as an electrolyte. The hybrid supercapacitor exhibited an excellent energy density of 108 Wh/kg at 1 A/g compared to 43 Wh/g at 1 A/g for the carbon-only supercapacitor.