Spatter formation is a major issue in deep penetration welding with solid-state lasers at high welding speeds above 8 m/min. In order to limit spatter formation, the use of local gas flows represents a technically feasible solution. By using the gas flow, the pressure balance inside the keyhole, and therefore the keyhole stability, is affected. Existing investigations demonstrate a reduction in spatter and pore formation for partial penetration welding up to a welding speed of 5 m/min. However, the effect of the gas flow is not yet clarified for full penetration welding at welding speeds above 8 m/min. By using a precisely adjustable shielding gas supply, the effect of a local gas flow of argon was characterized by welding stainless steel AISI304 (1.4301/X5CrNi18-10). The influence of the gas flow on the melt pool dynamics and spatter formation was recorded by means of high-speed videography and subsequently analyzed by image processing. Schlieren videography was used to visualize the forming flow flied. By the use of the gas, a change in melt pool dynamics and gas flow conditions was observed, correlating to a reduction in loss of mass up to 70%. Based on the investigations, a model of the acting effect mechanism was given.

Background. Spatter formation at melt pool swellings at the keyhole rear wall is a major issue for laser deep penetration welding at speeds beyond 8 m/min. A gas nozzle directed towards the keyhole, that supplies shielding gas locally, is advantageous in reducing spatter formation due to its simple utilization. However, the relationship between local gas flow, laser spot size, and the resulting effects on spatter formation at high welding speeds up to 16 m/min are not yet fully understood. Methods. The high-alloy steel AISI 304 (1.4301/X5CrNi18-10) was welded with laser spot sizes of 300 μm and 600 μm while using a specially designed gas nozzle directed to the keyhole. Constant welding depth was ensured by Optical Coherence Tomography (OCT). Spatter formation was evaluated by precision weighing of samples. Subsequent processing of high-speed images was used to evaluate spatter quantity, size, and velocity. The keyhole oscillation was determined by Fast Fourier Transform (FFT) analysis. Tracking the formation of melt pool swellings at the keyhole rear wall provided information on the upward melt flow velocity. Results. The local gas flow enabled a significant reduction in the number of spatters and loss of mass for both laser spot sizes and indicated an effect on surface tension by shielding the processing zone from the ambient atmosphere. The laser spot size affected the upward melt flow velocity and spatter velocity.

Partial shielding by means of local gas supply has proven to be very effective in reducing spatter. Besides the effect of gas-induced dynamic pressure, the shielding of oxygen is also highly relevant for melt pool dynamics and spatter formation due to the growth of oxides and the influence on surface tension. Therefore, this paper addresses the effect of local supplied argon on oxide growth and seam topography during keyhole mode laser beam welding of high-alloy steel AISI 304. To determine the shielding quality, the results are compared to laser beam welding in a global argon atmosphere. The topography of the upper weld seams was analyzed by scanning electron microscopy (SEM). An X-ray microanalysis (EDX) in line scan modus was performed to determine and to locate the elements which are covering the specimen surface. The chemical state of the found elements was quantified by X-ray photoelectron spectroscopy (XPS). In a last step, high-speed synchrotron X-ray imaging was performed to separate the effect of the gas-induced pressure and the gas-induced shielding on keyhole geometry. The results show that a local supply of argon contributes to a significant difference in oxide growth, affecting melt pool convection and weld seam geometry. It was further shown that the effect of gas flows at low flow rates is primarily because of oxygen shielding, as no significant difference in keyhole geometry was found by high-speed synchrotron X-ray imaging.

The development of adaptive and intelligent clamping devices allows for the reduction of rejects and defects based on weld discontinuities in laser-beam welding. The utilization of fixture-integrated sensors and actuators is a new approach, realizing adaptive clamping devices that enable in-process data acquisition and a time-dependent adjustment of process conditions and workpiece position by means of a closed-loop control. The present work focused on sensor and actuator integration for an adaptive clamping device utilized for laser-beam welding in a butt-joint configuration, in which the position and acting forces of the sheets to be welded can be adjusted during the process (studied welding speeds: 1 m/min, 5 m/min). Therefore, a novel clamping system was designed allowing for the integration of inductive probes and force cells for obtaining time-dependent data of the joint gap and resulting forces during welding due to the displacement of the sheets. A novel automation engineering concept allowed the communication between different sensors, actuators and the laser-beam welding setup based on an EtherCAT bus. The subsequent development of a position control and a force control and their combination was operated with a real time PC as master in the bus system and proved the feasibility of the approach based on proportional controllers. Finally, the scalability regarding higher welding speeds was demonstrated.