Bacterial cellulose (BC) is a biopolymer whose properties have been intensively studied, especially for biomedical applications. Since BC has no antimicrobial activity, it is necessary to use bioactive substances for developing wound healing applications. Another drawback of BC is the loss if its water retention capacity after dehydration. In order to overcome these problems, carboxymethyl cellulose (CMC) and turmeric extract (TE) were selected for the preparation of BC composites. Citric acid (CA) was used as the crosslinking agent. These composites were tested as potential antimicrobial wound dressing materials. TE-loaded BC–CMC composites were characterized in terms of their morphology, crystallinity, and thermal behavior. Swelling tests and curcumin-release kinetic analysis were also performed. All the composites tested had high swelling degrees, which is an advantage for the exudate adsorption from chronic wounds. The antibacterial potential of such composites was tested against Escherichia coli (E. coli), Staphylococcus aureus (S. aureus), and Candida albicans (C. albicans). The in vitro cytotoxicity toward L929 fibroblast cells was studied as well. The obtained results allow us to recommend these composites as good candidates for wound dressing applications.

Bacterial cellulose (BC) is a unique microbial biopolymer with a huge number of significant applications in the biomedical field, including bone tissue engineering. The present study proposes to obtain and characterize BC hybrid composites with calcium phosphate as biocompatible and bioactive membranes for bone tissue engineering. BC precursor membranes were obtained in static culture fermentation, and after purification, were oxidized to obtain 2,3-dialdehyde bacterial cellulose (DABC). Calcium phosphate-BC oxidized membranes were produced by successive immersion in precursor solutions under ultrasonic irradiation. The samples were characterized for their physicochemical properties using scanning electron microscopy (SEM) coupled with energy-dispersive X-ray spectroscopy, attenuated total reflectance-Fourier transform infrared (ATR-FTIR) spectroscopy grazing incidence X-ray diffraction (GI-XRD), solid-state ¹³C nuclear magnetic resonance (CP/MAS ¹³C NMR), and complex thermal analysis. In vitro cell studies were also performed to evaluate the influence of modified morphological characteristics on cell adhesion and proliferation. The results showed an increase in porosity and biodegradability for DABC hybrid composites compared with BC. In vitro cell studies have revealed that both hybrid composites favor cell adhesion to the surface. The new BC and DABC hybrid composites with calcium phosphate could be considered promising materials for bone tissue regeneration.