Recent advancements in biomedicine have focused on designing novel and stable interfaces that can drive a specific cellular response toward the requirements of medical devices or implants. Among these, in recent years, electroactive polymers (i.e., polyvinylidene fluoride or PVDF) have caught the attention within the biomedical applications sector, due to their insolubility, stability in biological media, in vitro and in vivo non-toxicity, or even piezoelectric properties. However, the main disadvantage of PVDF-based bio-interfaces is related to the absence of the functional groups on the fluoropolymer and their hydrophobic character leading to a deficiency of cell adhesion and proliferation. This work was aimed at obtaining hydrophilic functional PVDF polymer coatings by using, for the first time, the one-step, matrix-assisted pulsed evaporation (MAPLE) method, testing the need of a post-deposition thermal treatment and analyzing their preliminary capacity to support MC3T3-E1 pre-osteoblast cell survival. As osteoblast cells are known to prefer rough surfaces, MAPLE deposition parameters were studied for obtaining coatings with roughness of tens to hundreds of nm, while maintaining the chemical properties similar to those of the pristine material. The in vitro studies indicated that all surfaces supported the survival of viable osteoblasts with active metabolisms, similar to the “control” sample, with no major differences regarding the thermally treated materials; this eliminates the need to use a secondary step for obtaining hydrophilic PVDF coatings. The physical-chemical characteristics of the thin films, along with the in vitro analyses, suggest that MAPLE is an adequate technique for fabricating PVDF thin films for further bio-applications.

Osseous implantology’s material requirements include a lack of potential for inducing allergic disorders and providing both functional and esthetic features for the patient’s benefit. Despite being bioinert, Zirconia ceramics have become a candidate of interest to be used as an alternative to titanium dental and cochlear bone-anchored hearing aid (BAHA) implants, implying the need for endowing the surface with biologically instructive properties by changing basic parameters such as surface texture. Within this context, we propose anisotropic and isotropic patterns (linear microgroove arrays, and superimposed crossline microgroove arrays, respectively) textured in zirconia substrates, as bioinstructive interfaces to guide the cytoskeletal organization of human mesenchymal stem cells (hMSCs). The designed textured micro-nano interfaces with either steep ridges and microgratings or curved edges, and nanoroughened walls obtained by direct femtosecond laser texturing are used to evaluate the hMSC response parameters and osteogenic differentiation to each topography. Our results show parallel micro line anisotropic surfaces are able to guide cell growth only for the steep surfaces, while the curved ones reduce the initial response and show the lowest osteogenic response. An improved osteogenic phenotype of hMSCs is obtained when grown onto isotropic grid/pillar-like patterns, showing an improved cell coverage and Ca/P ratio, with direct implications for BAHA prosthetic development, or other future applications in regenerating bone defects.

Nowadays, using polymers with specific characteristics to coat the surface of a device to prevent undesired biological responses can represent an optimal strategy for developing new and more efficient implants for biomedical applications. Among them, zwitterionic phosphorylcholine-based polymers are of interest due to their properties to resist cell and bacterial adhesion. In this work, the Matrix-Assisted Laser Evaporation (MAPLE) technique was investigated as a new approach for functionalising Polydimethylsiloxane (PDMS) surfaces with zwitterionic poly(2-Methacryloyloxyethyl-Phosphorylcholine) (pMPC) polymer. Evaluation of the physical–chemical properties of the new coatings revealed that the technique proposed has the advantage of achieving uniform and homogeneous stable moderate hydrophilic pMPC thin layers onto hydrophobic PDMS without any pre-treatment, therefore avoiding the major disadvantage of hydrophobicity recovery. The capacity of modified PDMS surfaces to reduce bacterial adhesion and biofilm formation was tested for Gram-positive bacteria, Staphylococcus aureus (S. aureus), and Gram-negative bacteria, Escherichia coli (E. coli). Cell adhesion, proliferation and morphology of human THP-1 differentiated macrophages and human normal CCD-1070Sk fibroblasts on the different surfaces were also assessed. Biological in vitro investigation revealed a significantly reduced adherence on PDMS–pMPC of both E. coli (from 29 × 10 ⁶ to 3 × 10² CFU/mL) and S. aureus (from 29 × 10⁶ to 3 × 10² CFU/mL) bacterial strains. Additionally, coated surfaces induced a significant inhibition of biofilm formation, an effect observed mainly for E. coli. Moreover, the pMPC coatings improved the capacity of PDMS to reduce the adhesion and proliferation of human macrophages by 50% and of human fibroblast by 40% compared to unmodified scaffold, circumventing undesired cell responses such as inflammation and fibrosis. All these highlighted the potential for the new PDMS–pMPC interfaces obtained by MAPLE to be used in the biomedical field to design new PDMS-based implants exhibiting long-term hydrophilic profile stability and better mitigating foreign body response and microbial infection.

Designing and obtaining new synthetic smart biointerfaces with specific and controlled characteristics relevant for applications in biomedical and bioengineering domains represents one of the main challenges in these fields. In this work, Matrix-Assisted Pulsed Laser Evaporation (MAPLE) is used to obtain synthetic biointerfaces of poly(N-isopropyl acrylamide-butyl acrylate) p(NIPAM-BA) copolymer with different characteristics (i.e., roughness, porosity, wettability), and their effect on normal HEK 293 T and murine melanoma B16-F1 cells is studied. For this, the influence of various solvents (chloroform, dimethylsulfoxide, water) and fluence variation (250–450 mJ/cm²) on the morphological, roughness, wettability, and physico–chemical characteristics of the coatings are evaluated by atomic force microscopy, scanning electron microscopy, contact angle measurements, Fourier-transform-IR spectroscopy, and X-ray photoelectron spectroscopy. Coatings obtained by the spin coating method are used for reference. No significant alteration in the chemistry of the surfaces is observed for the coatings obtained by both methods. All p(NIPAM-BA) coatings show hydrophilic character, with the exception of those obtained with chloroform at 250 mJ/cm². The surface morphology is shown to depend on both solvent type and laser fluence and it ranges from smooth surfaces to rough and porous ones. Physico–chemical and biological analysis reveal that the MAPLE deposition method with fluences of 350–450 mJ/cm² when using DMSO solvent is more appropriate for bioengineering applications due to the surface characteristics (i.e., pore presence) and to the good compatibility with normal cells and cytotoxicity against melanoma cells.

In this work, thin films of lamellar clays were deposited by laser techniques (matrix assisted pulsed laser evaporation (MAPLE) and pulsed laser deposition (PLD)). The focus of this paper is the optimization of deposition parameters for the production of highly oriented crystalline films. The films were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), and scanning electron microscopy (SEM). Contact angle measurements were employed to identify the wetting properties of the deposited thin films. Hydrophobic to superhydrophilic films can be prepared by using different deposition techniques and deposition parameters. MAPLE led to superhydrophilic films with contact angles in the range 4°–8°, depending on the microstructure and surface roughness at micro and nano scale. The 1064 nm PLD had a high deposition rate and produced a textured film while at λ = 193 nm an extremely thin and amorphous layer was depicted. Oriented kaolinite films were obtained by MAPLE even at 5 wt.% kaolinite in the target.

Since breast cancer is one of the most common forms of cancer in women, silicone mammary implants have been extensively employed in numerous breast reconstruction procedures. However, despite the crucial role they play, their interaction with the host’s immune system and microbiome is poorly understood. Considering this, the present work investigates the immunomodulatory and bacterial mitigation potential of six textured surfaces, based on linear step-like features with various regular and irregular multiscaled arrangements, in comparison to a flat PDMS surface. We hypothesise that the chosen surface geometries are capable of modulating the cellular response through mechanical interdigitation within the multiscaled surface morphology, independent of the surface chemical properties. Each type of sample was characterised from a physico-chemical and biological points of view and by comparison to the flat PDMS surface. The overall results proved that the presence of linear multiscaled step-like features on the PDMS surface influenced both the surface’s characteristics (e.g., surface energy, wettability, and roughness parameters), as well as the cellular response. Thus, the biological evaluation revealed that, to different degrees, biomaterial-induced macrophage activation can be mitigated by the newly designed microtextured surfaces. Moreover, the reduction in bacteria adherence up to 90%, suggested that the topographical altered surfaces are capable of suppressing bacterial colonisation, therefore demonstrating that in a surgical environment at risk of bacterial contamination, they can be better tolerated.