The effect of nanostructure of PLD (Pulsed Laser Deposition)-deposited Pd/WO₃ sensing films on room temperature (RT) hydrogen sensing properties of SAW (Surface Acoustic Wave) sensors was studied. WO₃ thin films with different morphologies and crystalline structures were obtained for different substrate temperatures and oxygen deposition pressures. Nanoporous films are obtained at high deposition pressures regardless of the substrate temperature. At lower pressures, high temperatures lead to WO₃ c-axis nanocolumnar growth, which promotes the diffusion of hydrogen but only once H₂ has been dissociated in the nanoporous Pd layer. XRD (X-ray Diffraction) analysis indicates texturing of the WO₃ layer not only in the case of columnar growth but for other deposition conditions as well. However, it is only the predominantly c-axis growth that influences film sensing properties. Bilayers consisting of nanoporous Pd layers deposited on top of such WO₃ layers lead to good sensing results at RT. RT sensitivities of 0.12–0.13 Hz/ppm to hydrogen are attained for nanoporous bilayer Pd/WO₃ films and of 0.1 Hz/ppm for bilayer films with a nanocolumnar WO₃ structure. SAW sensors based on such layers compare favorably with WO₃-based hydrogen detectors, which use other sensing methods, and with SAW sensors with dense Pd/WO₃ bilayers.

Due to its physical and chemical properties, the n-type tungsten oxide (WO₃) semiconductor is a suitable photoanode for water decomposition reaction. The responses of the photoelectrochemical PEC water-splitting properties as an effect of structural and optical changes of WO₃ thin films, as well as the nature of electrolyte solutions, were studied in this work. The WO₃ thins films have been obtained by pulsed laser deposition (PLD) on silicon (Si(001)) covered with platinum substrates using three different laser wavelengths. As the XRD (X-ray diffraction) and XTEM (cross-section transmission electron microscopy) analysis shows, the formation of highly crystalline monocline WO₃ phase is formed for the film deposited at 1064 nm wavelength and poor crystalline phases with a large ordering anisotropy, characteristic of 2D structures for the films deposited at 355 nm and 193 nm wavelengths, respectively. The photogenerated current densities J_ph depend on the laser wavelength, in both alkaline and acidic electrolyte. The maximum values of the photocurrent density have been obtained for the sample prepared with laser emitting at 355 nm. This behavior can be correlated with the coherent crystallized atomic ordering that appear for long distances (10–15 nm) in the (001) plane of the monoclinic WO₃ phase structure films obtained at 355 nm laser wavelength. All the samples show poor current density in dark conditions and they are very stable in both acidic and alkaline solutions. The highest photocurrent density value is obtained in acidic solution for the WO₃ thin film prepared by 355 nm laser (29 mA/cm² at 1.6 V vs. RHE (1.35 V vs. Ag/AgCl)).

Tuning the intrinsic structural and stoichiometric properties by different means is used for increasing the green energy production efficiency of complex oxide materials. Here, we report on the formation of self-assembled nanodomains and their effects on the photoelectrochemical (PEC) properties of LaFeO₃ (LFO) epitaxial thin films as a function of layer’s thickness. The variation with the film’s thickness of the structural parameters such as in-plane and out-of-plane crystalline coherence length and the coexistence of different epitaxial orientation—SrTiO₃// LFO, SrTiO₃// LFO and [110] LFO//[10] STO, as well as the appearance of self-assembled nanodomains for film’s thicknesses higher than 14 nm, is presented. LFO thin films exhibit different epitaxial orientations depending on their thickness, and the appearance of self-assembled nanopyramids-like domains after a thickness threshold value has proven to have a detrimental effect on the PEC functional properties. Using Nb:SrTiO₃ as conductive substrate and 0.5 M NaOH aqueous solution for PEC measurements, the dependence of the photocurrent density and the onset potential vs. RHE on the structural and stoichiometric features exhibited by the LFO photoelectrodes are unveiled by the X-ray diffraction, high-resolution transmission electron microscopy, ellipsometry, and Rutherford backscattering spectroscopy results. The potentiodynamic PEC analysis has revealed the highest photocurrent density J_photocurrent values (up to 1.2 mA/cm²) with excellent stability over time, for the thinnest LFO/Nb:SrTiO₃ sample, both cathodic and anodic behavior being noticed. Noticeably, the LFO thin film shows unbiased hydrogen evolution from water, as determined by gas chromatography in aqueous 0.5 M NaOH solution under constant illumination.

Curcumin (CR) is a natural antioxidant compound extracted from Curcuma longa (turmeric). Until now, researches related to the incorporation of CR into layered double hydroxides (LDHs) were focused only on hybrid structures based on a MgxAl-LDH matrix. Our studies were extended towards the incorporation of CR in another type of LDH-matrix (Zn3Al-LDH) which could have an even more prolific effect on the antioxidant activity due to the presence of Zn. Four CR-modified Zn3Al-LDH solids were synthesized, e.g., PZn3Al-CR(Aq), PZn3Al-CR(Et), RZn3Al-CR(Aq) and RZn3Al-CR(Et) (molar ratio CR/Al = 1/10, where P and R stand for the preparation method (P = precipitation, R = reconstruction), while (Aq) and (Et) indicate the type of CR solution, aqueous or ethanolic, respectively). The samples were characterized by XRD, Attenuated Total Reflectance Fourier Transformed IR (ATR-FTIR) and diffuse reflectance (DR)-UV–Vis techniques and the CR-release was investigated in buffer solutions at different pH values (1, 2, 5, 7 and 8). XRD results indicated a layered structure for PZn3Al-CR(Aq), PZn3Al-CR(Et), RZn3Al-CR(Aq) impurified with ZnO, while RZn3Al-CR(Et) contained ZnO nano-particles as the main crystalline phase. For all samples, CR-release revealed a decreasing tendency towards the pH increase, and higher values were obtained for RZn3Al-CR(Et) and PZn3Al-CR(Et) (e.g., 45% and 25%, respectively at pH 1).

The combination of layered double hydroxides (LDH) with graphene oxide (GO) enables the formation of nanohybrids with improved properties. This work focuses on the structural and catalytic properties of Ce-containing MgAl LDH-GO composites bearing different concentrations of GO in the range of 5–25 wt.%. The synthesis of the composites was performed by co-precipitating the LDH phase in the presence of GO, while their characterization was performed using XRF, XRD, DRIFT, Raman, SEM, nitrogen adsorption-desorption, and acidity-basicity measurements. The LDH-GO composites, showing redox, basic, and acid catalytic functions, were tested in two different types of organic transformations: (i) Knoevenagel condensation and (ii) one-pot cascade oxidation-Knoevenagel condensation. (i) The cinnamic acid was synthesized by the Knoevenagel condensation of benzaldehyde with diethylmalonate. The composites showed catalytic performances in strong contrast to neat LDH or GO, suggesting a synergistic interaction between the two components. During Knoevenagel condensation, the catalytic activity increased with the GO content in the hybrids up to 15 wt.% and decreased afterwards. (ii) 2-Benzoyl-3-phenylacrylonitrile was synthesized by the aerobic oxidation of benzyl alcohol followed by the Knoevenagel condensation with benzoyl acetonitrile using three different non-polar solvents, i.e., toluene, benzene, and mesitylene. The conversion of benzyl alcohol was higher for the hybrid materials compared to the individual components but decreased with the increase of the graphene oxide concentration.

The strain engineering effects induced by different means, e.g., the substrate lattice mismatch and/or chemical doping, on the functional properties of perovskite thin films have triggered interest in the use of these materials in different applications such as energy storage/generation or photonics. The effects of the film’s thickness and strain state of the structure for the lead-free perovskite ferrite-based materials (BiFeO₃-BFO; Y-doped BiFeO₃-BYFO; LaFeO₃-LFO) on their functional properties are highlighted here. As was previously demonstrated, the dielectric properties of BFO epitaxial thin films are strongly affected by the film thickness and by the epitaxial strain induced by the lattice mismatch between substrate and film. Doping the BiFeO₃ ferroelectric perovskite with rare-earth elements or inducing a high level of structural deformation into the crystalline structure of LaFeO₃ thin films have allowed the tuning of functional properties of these materials, such as dielectric, optical or photocatalytic ones. These changes are presented in relation to the appearance of complex ensembles of nanoscale phase/nanodomains within the epitaxial films due to strain engineering. However, it is a challenge to maintain the same level of epitaxial strain present in ultrathin films (<10 nm) and to preserve or tune the positive effects in films of thicknesses usually higher than 30 nm.