Formation of regularities of the nanometric oxide precipitates and defect microstructure in vanadium-based low activation alloys V–Cr–Zr–(C,N,O) and V–Cr–W–Zr–(C,N,O) as a function of the regimes of their thermochemical treatment was investigated. Several methods of internal oxidation which provide formation of the nanosized ZrO2 particles of controllable dispersion, ensure the nanometric size of the heterophase structure to be maintained up to the temperatures as high as 1300–1400 °С, and allow the recrystallization temperature to be increased up to ≥1400 °С were proposed. Formation of such microstructure contributes to dispersion- and substructural hardening and results in more than twofold increase in the yield stress of these alloys both at room and elevated (800 °С) temperatures, compared to the conventional thermo-mechanical treatment

In this paper, the structural characteristics of a W-Ta-Mo-Nb-V-Cr-Zr-Ti non-equiatomic refractory metal alloy obtained by spark plasma sintering (SPS) of a high-energy ball-milled powder mixture are reported. High-energy ball milling resulted in the formation of particle agglomerates ranging from several tens to several hundreds of micrometers. These agglomerates were composed of micrometer and submicrometer particles. It was found that, during ball milling, a solid solution of A2 structure formed. The grains of the sintered material ranged from fractions of a micrometer to several micrometers. During SPS, the phase transformations in the alloy led to the formation of a Laves phase of C15 structure and ZrO and ZrO₂ nanoparticles. The microhardness of the ball-milled alloy and sintered material was found to be 9.28 GPa ± 1.31 GPa and 8.95 GPa ± 0.42 GPa, respectively. The influence of the processing conditions on the structure, phase composition, and microhardness of the alloy is discussed.

The paper studies the effect of the annealing temperature on microstructural transformation and micro-hardness variation in an internally oxidized vanadium alloy V—Cr—ZrO2deformed by high-pressure...