Three-dimensional printing (3DP) of thermoplastic polyurethane (TPU) is gaining interest in the medical industry thanks to the combination of tunable properties that TPU exhibits and the possibilities that 3DP processes offer concerning precision, time, and cost of fabrication. We investigated the implementation of a medical grade TPU by fused deposition modelling (FDM) for the manufacturing of an implantable medical device from the raw pellets to the gamma (γ) sterilized 3DP constructs. To the authors’ knowledge, there is no such guide/study implicating TPU, FDM 3D-printing and gamma sterilization. Thermal properties analyzed by differential scanning calorimetry (DSC) and molecular weights measured by size exclusion chromatography (SEC) were used as monitoring indicators through the fabrication process. After gamma sterilization, surface chemistry was assessed by water contact angle (WCA) measurement and infrared spectroscopy (ATR-FTIR). Mechanical properties were investigated by tensile testing. Biocompatibility was assessed by means of cytotoxicity (ISO 10993-5) and hemocompatibility assays (ISO 10993-4). Results showed that TPU underwent degradation through the fabrication process as both the number-averaged (Mn) and weight-averaged (Mw) molecular weights decreased (7% Mn loss, 30% Mw loss, p < 0.05). After gamma sterilization, Mw increased by 8% (p < 0.05) indicating that crosslinking may have occurred. However, tensile properties were not impacted by irradiation. Cytotoxicity (ISO 10993-5) and hemocompatibility (ISO 10993-4) assessments after sterilization showed vitality of cells (132% ± 3%, p < 0.05) and no red blood cell lysis. We concluded that gamma sterilization does not highly impact TPU regarding our application. Our study demonstrates the processability of TPU by FDM followed by gamma sterilization and can be used as a guide for the preliminary evaluation of a polymeric raw material in the manufacturing of a blood contacting implantable medical device.

The effect of the post-annealing process on different properties of poly (L-lactic acid) (PLLA) nanofibers has been investigated in view of their use in energy-harvesting devices. Polymeric PLLA nanofibers were prepared by using electrospinning and then were thermally treated above their glass transition. A detailed comparison between as-spun (amorphous) and annealed (semi-crystalline) samples was performed in terms of the crystallinity, morphology and mechanical as well as piezoelectric properties using a multi-technique approach combining DSC, XRD, FTIR, and AFM measurements. A significant increase in the crystallinity of PLLA nanofibers has been observed after the post-annealing process, together with a major improvement of the mechanical and piezoelectric properties.