Nanoparticles are defined as ultrafine particles sized between 1 and 100 nanometres in diameter. In recent decades, there has been wide scientific research on the various uses of nanoparticles in construction, electronics, manufacturing, cosmetics, and medicine. The advantages of using nanoparticles in construction are immense, promising extraordinary physical and chemical properties for modified construction materials. Among the many different types of nanoparticles, titanium dioxide, carbon nanotubes, silica, copper, clay, and aluminium oxide are the most widely used nanoparticles in the construction sector. The promise of nanoparticles as observed in construction is reflected in other adoptive industries, driving the growth in demand and production quantity at an exorbitant rate. The objective of this study was to analyse the use of nanoparticles within the construction industry to exemplify the benefits of nanoparticle applications and to address the short-term and long-term effects of nanoparticles on the environment and human health within the microcosm of industry so that the findings may be generalised. The benefits of nanoparticle utilisation are demonstrated through specific applications in common materials, particularly in normal concrete, asphalt concrete, bricks, timber, and steel. In addition, the paper addresses the potential benefits and safety barriers for using nanomaterials, with consideration given to key areas of knowledge associated with exposure to nanoparticles that may have implications for health and environmental safety. The field of nanotechnology is considered rather young compared to established industries, thus limiting the time for research and risk analysis. Nevertheless, it is pertinent that research and regulation precede the widespread adoption of potentially harmful particles to mitigate undue risk.

Cigarette butts (CBs) are the most commonly littered waste material in the world. It is estimated that over 5.7 trillion cigarettes are consumed worldwide each year. Consequently, millions of tonnes of highly toxic waste are contaminating the environment. CBs are composed of cellulose acetate filters—a polymer with poor biodegradability—and which, depending upon the environmental conditions, can take many years to decompose. In this study, fired clay bricks were manufactured with 0.5%, 1%, 1.5%, and 2% CBs by mass and tested against control bricks with 0% CBs. The results revealed a decrease in compressive strength from 48.6 MPa for 0% CB content bricks to 30.8 MPa for 1% CB content bricks, and a decrease in dry density with the increase in CB content, from 2114 kg/m³ for the control bricks to 1983 kg/m³ and 1969 kg/m³ for 1% and 2% CB content bricks. The highest value of water absorption appeared for 2% CB content bricks, which reached an absorption rate of 13.1% compared to 9% for the control bricks. The energy required during the firing process was calculated with a saving of up to 10.20%, for bricks incorporating 1% CBs. The thermal conductivity of the samples showed a reduction of 17% from 1.078 to 0.898 W m⁻¹·K⁻¹ with the addition of 1% CBs. In addition, the manufactured bricks were tested for efflorescence, an initial rate of absorption (IRA), microstructural analysis, and shrinkage. A life-cycle assessment (LCA) is recommended to analyze the environmental impacts of bricks incorporating CBs.