The state of laser processing in surface materials modification in Poland is reported, based on own experience, coworkers and coauthors results, as well the literature review. The curriculum concerning historical development of lasers and laser technology in Poland, laser-matter interaction, as well basis of different laser techniques applied in materials surface engineering (solid state hardening, melting, alloying, cladding, ablation, shot peening, cleaning and texturing) are reviewed, and compared with results of coauthors, as well with a wide range of Polish authors papers. Finally, it is concluded that overall state of research on laser application in surface engineering in Poland is well developed and still growing industrial application is observed.

A high power direct diode laser, emitting in the range of near infrared radiation at wavelength 808–940 nm, was applied to produce a titanium matrix composite on a surface layer of titanium alloy Ti6Al4V by laser surface gas nitriding. The nitrided surface layers were produced as single stringer beads at different heat inputs, different scanning speeds, and different powers of laser beam. The influence of laser nitriding parameters on the quality, shape, and morphology of the surface layers was investigated. It was found that the nitrided surface layers consist of titanium nitride precipitations mainly in the form of dendrites embedded in the titanium alloy matrix. The titanium nitrides are produced as a result of the reaction between molten Ti and gaseous nitrogen. Solidification and subsequent growth of the TiN dendrites takes place to a large extent at the interface of the molten Ti and the nitrogen gas atmosphere. The direction of TiN dendrites growth is perpendicular to the surface of molten Ti. The roughness of the surface layers depends strongly on the heat input of laser nitriding and can be precisely controlled. In spite of high microhardness up to 2400 HV0.2, the surface layers are crack free.

The autogenous laser welding of 2.5 mm thick butt joints of thermomechanically rolled fine-grain steel grade S420MC was investigated. Butt joints were laser welded by the Yb:YAG Disk laser, emitted a circular laser beam with spot diameter of 200 μm at 1.03 μm wavelength, and also by the high power direct diode laser, emitted a rectangular beam with dimension of 1.8x6.8 mm at 808 nm wavelength. Different welding modes were identified for the lasers applied. The conduction welding mode was observed in whole of the diode laser welding parameters. While high quality joints, without any internal defects and characterized with satisfactory mechanical performance were produced in a wide range of parameters. The butt joints produced by Disk laser were welded at keyhole mode. In this case a slight tendency to weld porosity was found.

The article presents results of investigations on autogenous laser welding of new grade STRENX 1100 MC steel. The modern Disk laser was applied for of 5.0 mm thick butt joints welding. The influence of laser welding parameters, mainly the energy input of laser welding on the penetration shape, weld quality, structure and mechanical performance was investigated. It was found that the investigated steel has surprisingly low carbon equivalent CET just 0.328, and also relatively high temperature of martensitic transformation M_sat 430.6°C. Despite very rapid cooling times t_8/5in a range from 0.6 to 1.3 s, thus rapid solidification there was no tendency to cracking of weld metal or HAZ. Significant drop of microhardness in the HAZ resulted in a decrease of tensile strength of joints, compared to the base metal. Impact toughness of test joints was at only 50÷60% of the base metal.

In order to improve the tribological properties of titanium alloy Ti6Al4V composite surface layers Ti/TiN were produced during laser surface gas nitriding by means of a novel high power direct diode laser with unique characteristics of the laser beam and a rectangular beam spot. Microstructure, surface topography and microhardness distribution across the surface layers were analyzed. Ball-on-disk tests were performed to evaluate and compare the wear and friction characteristics of surface layers nitrided at different process parameters, base metal of titanium alloy Ti6Al4V and also the commercially pure titanium. Results showed that under dry sliding condition the commercially pure titanium samples have the highest coefficient of friction about 0.45, compared to 0.36 of titanium alloy Ti6Al4V and 0.1-0.13 in a case of the laser gas nitrided surface layers. The volume loss of Ti6Al4V samples under such conditions is twice lower than in a case of pure titanium. On the other hand the composite surface layer characterized by the highest wear resistance showed almost 21 times lower volume loss during the ball-on-disk test, compared to Ti6Al4V samples

The following article describes results of investigations on influence of laser welding parameters on the weld shape, quality and mechanical properties of 2.0 mm thick butt joints of titanium alloy Ti6Al4V (Grade 5 according to ASTM B265) welded with a new generation disk laser TRUMPF TRUDISK 3302, emitting at 1030 nm, with maximum output power 3300 W at circular laser beam spot, characterized by laser beam divergence 8.0 mm•mrad. The test butt joints of Ti6Al4V titanium alloy sheets were prepared as single square groove (I-type joint) and one-side laser welded without an additional material, at a flat position, using a specially designed system for shielding gas (purity 99.999%). The investigations at the initial stage were focused on detailed analysis of influence of the basic laser welding parameters such as laser power and welding speed on the shape and quality of single bead produced during bead-on-plate welding. Then the optimal parameters were chosen for laser welding of 2.0 mm thick butt joints of the titanium alloy Ti6Al4V. Edges of the titanium alloy sheets were melted in argon atmosphere by the laser beam focused on the top surface of butt joints. The test welded joints were investigated by visual inspection, metallographic examinations, hardness and micro-hardness measurements and mechanical tests such as tensile tests and bending tests. It was found that the welding mode is a keyhole welding and providing high quality of joints requires a special techniques and conditions of laser welding, as well as special gas shielding nozzles is required.