In this paper, the influence of different fiber materials on the dynamic splitting mechanical properties of concrete was investigated. Brazil disc dynamic splitting tests were conducted on plain concrete, palm fiber-reinforced concrete, and steel fiber-reinforced concrete specimens using a split Hopkinson pressure bar (SHPB) test device with a 100 mm diameter and a V2512 high-speed digital camera. The Digital Image Correlation (DIC) technique was used to analyze the fracture process and crack propagation behavior of different fiber-reinforced concrete specimens and obtain their dynamic tensile properties and energy dissipation. The experimental results indicate that the addition of fibers can enhance the impact toughness of concrete, reduce the occurrence of failure at the loading end of specimens due to stress concentration, delay the time to failure of specimens, and effectively suppress the expansion of cracks. Steel fibers exhibit a better crack-inhibiting effect on concrete compared to palm fibers. The incident energy for the three types of concrete specimens is roughly the same under the same impact pressure. Compared with plain concrete, the energy absorption rate of palm fiber concrete is decreased, while that of steel fiber concrete is increased. Palm fiber-reinforced concrete and steel fiber-reinforced concrete have lower peak strains than plain concrete under the same loading duration. The addition of steel fibers significantly impedes the internal cracking process of concrete specimens, resulting in a relatively slow growth of damage variables.

Concrete cracking caused by corrosion of reinforcement could significantly shorten the durability of reinforced concrete structure. It remains critical to investigate the process and mechanism of the corrosion occurring to concrete reinforcement and establish the theoretical prediction model of concrete expansion force for the whole process of corrosion cracking of reinforcement. Under the premise of uniform corrosion of reinforcing steel bars, the elastic mechanics analysis method is adopted to analyze the entire process starting from the corrosion of steel bars to the cracking of concrete due to corrosion. A relationship model between the expansion force of corrosion of steel bars and the surface strain of concrete is established. On the cuboid reinforced concrete specimens with square cross-sections, accelerated corrosion tests are carried out to calibrate and verify the established model. The model can be able to estimate the real-time expansion force of reinforced concrete at any time of the whole process from the initiation of steel corrosion to the end of concrete cracking by measuring the surface strain of concrete. It could be useful for quantitative real-time monitoring of steel corrosion in concrete structures.

When operating within the environments rich with sodium chloride, steel bars of reinforced concrete structures are often subject to corrosion caused by surrounding erosive materials, and the associated rust expansion force due to corrosion takes a critical role in determining the durability of relevant reinforced concrete structures. By investigating the corrosion course of steel reinforcement with theory of elasticity, a numerical rust expansion model is established for the moment of concrete surface rupture based on non-uniform sin function. Cuboid reinforced concrete specimen with squared cross sections is tested to analyze the rust expansion when concrete cracks due to corrosive forces. The utility of the established expansion model is validated by numerical simulation with Abaqus through the comparison between the associated outcomes. The impacts of steel bar diameter and concrete cover thickness on the magnitude of rust expansion force are discussed.

The mechanical behaviors of granular materials are governed by the grain properties and microstructure of the materials. We conducted experiments to study the force transmission in granular materials using plane strain tests. The large amount of nearly continuous displacement data provided by the advanced noncontact experimental technique of digital image correlation (DIC) has provided a means to quantify local displacements and strains at the particle level. The average strain of each particle could be calculated based on the DIC method, and the average stress could be obtained using Hooke’s law. The relationship between the stress and particle force could be obtained based on basic Newtonian mechanics and the balance of linear momentum at the particle level. This methodology is introduced and validated. In the testing procedure, the system is tested in real 2D particle cases, and the contact forces and force chain are obtained and analyzed. The system has great potential for analyzing a real granular system and measuring the contact forces and force chain.