ZnO nanoparticles (NPs) synthesized by pulsed laser ablation (PLAL) of a zinc plate in deionized water were investigated by time-resolved photoluminescence (PL) and complementary techniques (TEM, AFM, μRaman). HRTEM images show that PLAL produces crystalline ZnO NPs in wurtzite structure with a slightly distorted lattice parameter a. Consistently, optical spectra show the typical absorption edge of wurtzite ZnO (E_g = 3.38 eV) and the related excitonic PL peaked at 3.32 eV with a subnanosecond lifetime. ZnO NPs display a further PL peaking at 2.2 eV related to defects, which shows a power law decay kinetics. Thermal annealing in O₂ and in a He atmosphere produces a reduction of the A₁(LO) Raman mode at 565 cm⁻¹ associated with oxygen vacancies, accompanied by a decrease of defect-related emission at 2.2 eV. Based on our experimental results the emission at 2.2 eV is proposed to originate from a photo-generated hole in the valence band recombining with an electron deeply trapped in a singly ionized oxygen vacancy. This investigation clarifies important aspects of the photophysics of ZnO NPs and indicates that ZnO emission can be controlled by thermal annealing, which is important in view of optoelectronic applications.

We report an experimental investigation by Raman spectroscopy of the decomposition process of Metal-Organic Framework (MOF) HKUST-1 upon exposure to air moisture (T=300 K, 70% relative humidity). The data collected here are compared with the indications obtained from a model of the process of decomposition of this material proposed in literature. In agreement with that model, the reported Raman measurements indicate that for exposure times longer than 20 days relevant irreversible processes take place, which are related to the occurrence of the hydrolysis of Cu-O bonds. These processes induce small but detectable variations of the peak positions and intensities of the main Raman bands of the material, which can be related to Cu-Cu, Cu-O, and O-C-O stretching modes. The critical analyses of these changes have permitted us to obtain a more detailed description of the process of decomposition taking place in HKUST-1 upon interaction with moisture. Furthermore, the reported Raman data give further strong support to the recently proposed model of decomposition of HKUST-1, contributing significantly to the development of a complete picture of the properties of this considerable deleterious effect.