Lead is a heavy metal that is bio accumulative and non-biodegradable that poses a threat to our health when it exists in excess in our bloodstream. It has found its way into wastewater from mostly chemical industrial processes. In this article, we investigated the adsorption and hence removal of lead (II) ions from wastewater in order to purify it for re-use in industrial processes or for plant and animal use. We synthesized nano silica hollow spheres (NSHS) and used them as adsorbents to remove lead ions from wastewater. When we characterized the NSHS using X-Ray diffraction, the amorphous nature of silica was evident with average crystal size of 39.5 nm. Scanning electron microscopy was used to determine the morphology of the adsorbent and the particles were found to be spherical in shape within a size range of 100–200 nm. Thermogravimetric analysis was used to determine the mass loss of NSHS which was ~2% at 800 °C. Our experimental results from adsorption studies showed that there was a linear relationship between temperature (27–60 °C) and adsorption efficiency and an inverse relationship between initial metal concentration (50–300 mg/L) and adsorption efficiency. At a maximum temperature of 60 °C and maximum initial metal concentration of 300 mg/L, the adsorption capacity was 200 mg/g and 262 mg/g, respectively while the adsorption efficiency was 99.6% and 87.4%, respectively. Our equilibrium and thermodynamic results revealed that the process was better modelled by the Langmuir adsorption isotherm (qmax = 266.89 mg/g and b = 0.89 L/mg). The adsorption process was both endothermic (ΔH = 97 kJ/mol) and spontaneous (ΔG = -22 kJ/mol). We can conclude that we were able to successfully synthesize NSHS, use them to remove lead (II) ions and the produced NSHS have a capacity that is higher than most other adsorbents investigated by other researchers.

The bioenergy production potential from biomasses is dependent on their characteristics. This study characterized pine sawdust samples from Zimbabwe and acacia tortilis samples from Botswana using conventional and spectrometry techniques. The ultimate analysis results for pine were 45.76% carbon (C), 5.54% hydrogen (H), 0.039% nitrogen (N), 0% sulphur (S) and 48.66% oxygen (O) and, for acacia, were 41.47% C, 5.15% H, 1.23% N, 0% S and 52.15% O. Due to the low N and S in the biomasses, they promise to provide cleaner energy than fossil-based sources. Proximate analysis results, on a dry basis, for acacia were 3.90% ash, 15.59% fixed carbon and 76.51% volatiles matter and 0.83%, 20% and 79.16%, respectively, for pine. A calorific value of 17.57 MJ/kg was obtained for pine, compared with 17.27 MJ/kg for acacia, suggesting they are good thermochemical feedstocks. Acacia’s bulk energy density is five times that of pine, making it excellent for compressed wood applications. Though the ash content in acacia was much higher than in pine, it fell below the fouling and slagging limit of 6%. In pyrolysis, however, high ash contents lead to reduced yields or the quality of bio-oil through catalytic reactions. Fourier transform infrared spectrometry indicated the presence of multiple functional groups, as expected for a biomass and its derivatives.

We collected pine dust and Acacia tortilis samples from Zimbabwe and Botswana, respectively. We then pyrolyzed them in a bench-scale plant under varying conditions. This investigation aimed to determine an optimum temperature that will give result to maximum yield and quality of the bio-oil fraction. Our experimental results show that we obtain the maximum yield of the oil fraction at a pyrolysis temperature of 550 °C for the acacia and at 500 °C for the pine dust. Our results also show that we obtain an oil fraction with a heating value (HHV) of 36.807 MJ/kg using acacia as the feed material subject to a primary condenser temperature of 140 °C. Under the same pyrolysis temperature, we obtain an HHV value of 15.78 MJ/kg using pine dust as the raw material at a primary condenser temperature of 110 °C. The bio-oil fraction we obtain from Acacia tortilis at these condensation temperatures has an average pH value of 3.42 compared to that of 2.50 from pine dust. The specific gravity of the oil from Acacia tortilis is 1.09 compared to that of 1.00 from pine dust. We elucidated that pine dust has a higher bio-oil yield of 46.1% compared to 41.9% obtained for acacia. Although the heavy oils at condenser temperatures above 100 °C had good HHVs, the yields were low, ranging from 2.8% to 4.9% for acacia and 0.2% to 12.7% for pine dust. Our future work will entail efforts to improve the yield of the heavy oil fraction and scale up our results for trials on plant scale capacity.

Contamination of water bodies by heavy metal ions is a challenge many developing nations like Zimbabwe face, with negative environmental and socio-economic repercussions. Treating affected bodies usually requires a costly consignment of chemicals and activated carbon. This research investigates the possible use of an abundant waste resource – poultry feathers – to make activated carbon for heavy metal ion removal. Poultry consumption in this nation generates more than five million tonnes of feathers a year, with very few uses of this by-product. This research was carried out to evaluate the effectiveness of activated carbon synthesized from poultry feathers with sodium hydroxide as the activating agent. It was tested for removing heavy metal ions from waste water at Lake Chivero and the experimental work done showed that it had a removal efficiency as high as 97%, with a high affinity for lead ions as compared with chromium ions. Upon characterization, the activated carbon showed an iodine number of 520 mg and it worked best at a pH value of 8. The efficiency removal also increased with increasing adsorbent concentration as well as contact time up to a period where these factors ceased to be the limiting factors of the reaction.