Pervious concrete is considered to be porous concrete because of its pore structure and excellent permeability. In general, larger porosity will increase the permeability coefficient, but will significantly decrease the compressive strength. The effects of water-cement ratio, fiber types, and fiber content on the permeability coefficient, porosity, compressive strength, and flexural strength were investigated. The pore tortuosity of the pervious concrete was determined by volumetric analysis and two-dimensional cross-sectional image analysis. The concept and calculation method of porosity tortuosity were further proposed. Results show that the permeability coefficient of the pervious concrete is the most suitable with a water-cement ratio of 0.30; the water permeability of the pervious concrete is influenced by fiber diameter. The permeability coefficient of pervious concrete with polypropylene thick fiber (PPTF) is greater than that with copper coated steel fiber (CCF) and the polypropylene fiber (PPF). The permeability coefficient is related to tortuosity and porosity, but when porosity is the same, the permeability coefficient may be different. Finally, general relations between the permeability coefficient and porosity tortuosity are constructed.

This research investigated the flexural behavior of high-strength concrete beams reinforced with continuous basalt fiber-reinforced polymer (BFRP) bars and discrete steel fibers. Five concrete beams with the dimensions of 150 × 300 × 2100 mm³ were constructed and tested to failure under four-point bending cyclic loading. The specimens consisted of four BFRP-reinforced concrete beams with various reinforcement ratios (ρ_f), namely, 0.56%, 0.77%, 1.15%, and 1.65%, and one conventional steel-reinforced concrete beam for comparison purposes. The cracking behavior, failure modes, load-deflection behavior, residual deformation, and stiffness degradation of the beams were studied. Additionally, a deformation-based approach was used to analyze the deformability of the beams. The results show that an increase in the ρ_f effectively restrained the crack widths, deflections, and residual deformation while also enhancing the flexural bearing capacity of the beams. In comparison to the first displacement cycle, the bearing capacity dropped by 10% on average in the third cycle. The stiffness exhibited a fast to slow degradation trend until failure. The residual stiffnesses were higher in beams with a higher ρ_f. The over-reinforced beams had superior deformability than the under-reinforced beams, according to the deformability factors.

The behavior of steel fiber concrete, which is the most widely used building material, has been widely examined. However, methods for calculating Fracture parameters differ by fracture behavior of SFHSC with different strengths. In this study, the fracture behavior of steel-fiber-reinforced high-strength concrete (SFHSC) was -investigated using three-point bending tests. A total of 144 notched concrete beams with a size of 100 mm × 100 mm × 515 mm were tested for three-point bending in 26 groups. The effects of the steel fiber volume ratio, steel fiber type, and relative notch depth on the fracture toughness (K_IC) and fracture energy (G_F) of SFHSC specimens were studied. The results show that an increase in the volume fraction of steel fiber (ρ_f) added to high-strength concrete (HSC) significantly improves the fracture behavior of HSC. As compared to milled and sheared corrugated steel fibers, cut bow steel fibers significantly improve the fracture behavior of SFHSC. The effect of incision depth changes on the K_IC and G_F of SFHSC and HSC for the comparison group has no common characteristics. With an increase in incision depth, the values of K_IC of the SFHSC specimens decrease slightly. The G_F0.5/G_F0.4 of the SFHSC specimens show a decreasing trend with an increase in ρ_f. According to the test results, we propose calculation models for the fracture behavior of SFHSC with different strengths. Thus, we present a convenient and accurate method to calculate fracture parameters, which lays a foundation for subsequent research.