The effects of tidal cycles associated with the water level on the biocorrosion of stainless steel AISI 316L were studied. Steel coupons were exposed to different conditions of immersion in mesocosms fed by fresh seawater either continuously or in accordance with the periodicity of natural tides. After 5 and 15 weeks, all coupons were found to have undergone ennoblement associated with the formation of a biofilm. Analysis of the composition of the bacterial community using denaturing gradient gel electrophoresis (DGGE) revealed differences in the biological succession. After 15 weeks, exposure to the simulated tidal conditions resulted in biofilms with lesser bacterial richness; the corresponding rate of corrosion, as determined by weight loss, was about 40 times lower compared to the case for the continuous exposure to seawater. Phylogenetic analysis of selected DGGE bands and the inspection of biofilm morphologies revealed that the faster rate of corrosion was associated with the presence of iron-oxidizing Zetaproteobacteria and eukaryotic photosynthetic microorganisms. On the other hand, intermittent exposure to seawater resulted in the succession of microorganisms resistant to the stress associated with sudden environmental changes, which was associated with a low rate of corrosion.

Microbial electrochemical technologies have revealed the opportunity of electrochemical enrichment for specific bacterial groups that are able to catalyze reactions of interest. However, there are unsolved challenges towards their application under aggressive environmental conditions, such as in the sea. This study demonstrates the impact of surface electrochemical potential on community composition and its corrosivity. Electrochemical bacterial enrichment was successfully carried out in natural seawater without nutrient amendments. Experiments were carried out for ten days of exposure in a closed-flow system over 316L stainless steel electrodes under three different poised potentials (−150 mV, +100 mV, and +310 mV vs. Ag/AgCl). Weight loss and atomic force microscopy showed a significant difference in corrosion when +310 mV (vs. Ag/AgCl) was applied in comparison to that produced under the other tested potentials (and an unpoised control). Bacterial community analysis conducted using 16S rRNA gene profiles showed that poised potentials are more positive as +310 mV (vs. Ag/AgCl) resulted in strong enrichment for Rhodobacteraceae and Sulfitobacter. Hence, even though significant enrichment of the known electrochemically active bacteria from the Rhodobacteraceae family was accomplished, the resultant bacterial community could accelerate pitting corrosion in 316 L stainless steel, thereby compromising the durability of the electrodes and the microbial electrochemical technologies.

Biofouling in membrane filtration systems poses significant operational challenges, leading to decreased permeate flux. The aim of this work was to study the anti-biofilm properties of new nanofiltration membranes produced via layer-by-layer, LBL, assembly by coating a polyvinylidene fluoride (PVDF) support with a polyethylenimine (PEI) and poly(acrylic acid)/graphene oxide (PAA-GO) mixture. The membranes were characterized according to contact angle, scanning electron microscopy (SEM), atomic force microscopy and their Z-potential. Biofilm quantification and characterization were carried out using crystal violet staining and SEM, while bacterial viability was assessed by using colony-forming units. The membrane with three bilayers ((PAA-PEI)3/PVDF) showed a roughness of 77.78 nm. The incorporation of GO ((GO/PAA-PEI)3/PVDF) produced a membrane with a smoother surface (roughness of 26.92 nm) and showed salt rejections of 16% and 68% for NaCl and Na2SO4, respectively. A significant reduction, ranging from 82.37 to 77.30%, in biofilm formation produced by S. aureus and E. coli were observed on modified membranes. Additionally, the bacterial viability on the modified membranes was markedly reduced (67.42–99.98%). Our results show that the modified membranes exhibited both antibiofilm and antimicrobial capacities, suggesting that these properties mainly depend on the properties of the modifying agents, as the initial adherence on the membrane surface was not totally suppressed, but the proliferation and formation of EPSs were prevented.

Characterizing seasonal changes in diatom community profiles in coastal environments is scarce worldwide. Despite diatoms being prevalent in microfouling, their role in microbially influenced corrosion of metallic materials remains poorly understood. This study reports the effect of seasonal variations on the settlement of marine diatoms and corrosion of 316 L stainless steel surfaces exposed to Chilean coastal seawater. Electron microscopy imaging revealed a diverse assembly of diatoms, exhibiting pronounced differences at genus level between summer and winter seasons, with a significant delay in diatom settlement during winter. Electrochemical measurements indicated an active role of diatoms in increasing corrosion current during biofilm development. While the final diatom composition was similar irrespective of the season, the analyses of diatom assemblages over time differed, showing faster colonization when silicate and nitrate were available. This study lays the foundation for future research on the dominant season-specific genera of diatoms to unveil the microbial interactions that could contribute to corrosion and to evaluate their potential as bioindicators for alternative surveillance strategies.

Antarctic marine sponges are essential components of the benthic fauna, playing a crucial role both through their own biological activities and their symbiotic relationships with diverse microorganisms. Yet, the transcriptional repertoire and the immune responses associated with interactions with microorganisms in this unique environment still need to be fully understood. Here, we investigated the transcriptional repertoire underlying the immune system processes of the Antarctic sponge Myxilla ( Burtonanchora ) lissostyla . We generated a de novo transcriptome and functional annotation for M. ( B. ) lissostyla , collected during the austral summer of 2019, 2020, and 2021. Our findings revealed an extensive transcriptional repertoire with a high and consistent expression of constitutive transcripts across the years. Key pathways related to immune response and homeostasis were the most expressed in the Antarctic sponge transcriptome, and a diverse array of immune receptors highlights the wide host immune repertoire. Low microbial abundance sponges share a vast repertoire of immune receptors, and a predominance of membrane‐bound PRRs was detected mainly in M . ( B. ) lissostyla , indicating a broad range of receptors available for initial interactions and engagement with microorganisms. The functional repertoire unveiled here establishes baselines for assessing potential functional changes that may arise due to climate change.