Tissue-engineered scaffolds are an effective method for the treatment of bone defects, and their structure and function are essential for bone regeneration. Digital light processing (DLP) printing technology has been widely used in bone tissue engineering (BTE) due to its high printing resolution and gentle printing process. As commonly used bioinks, synthetic polymers such as polyethylene glycol diacrylate (PEGDA) and Pluronic F127 diacrylate (F127DA) have satisfactory printability and mechanical properties but usually lack sufficient adhesion to cells and tissues. Here, a compound BTE scaffold based on PEGDA, F127DA, and gelatin methacrylate (GelMA) was successfully prepared using DLP printing technology. The scaffold not only facilitated the adhesion and proliferation of cells, but also effectively promoted the osteogenic differentiation of mesenchymal stem cells in an osteoinductive environment. Moreover, the bone tissue volume/total tissue volume (BV/TV) of the GelMA/PEGDA/F127DA (GPF) scaffold in vivo was 49.75 ± 8.50%, higher than the value of 37.10 ± 7.27% for the PEGDA/F127DA (PF) scaffold and 20.43 ± 2.08% for the blank group. Therefore, the GPF scaffold prepared using DLP printing technology provides a new approach to the treatment of bone defects.

Microglia, as the resident immune cells and first responder to neurological insults, play an extremely important role in the pathophysiological process of spinal cord injury. On the one hand, microglia respond rapidly and gather around the lesion in the early stage of injury to exert a protective role, but with the continuous stimulation of the injury, the excessive activated microglia secrete a large number of harmful substances, aggravate the injury of spinal cord tissue, and affect functional recovery. The effects of microglia depletion on the repair of spinal cord injury remain unclear, and there is no uniformly accepted paradigm for the removal methods and timing of microglia depletion, but different microglia depletion strategies greatly affect the outcomes after spinal cord injury. Therefore, this review summarizes the physiological and pathological roles of microglia, especially the effects of microglia depletion on spinal cord injury—sustained microglial depletion would aggravate injury and impair functional recovery, while the short-term depletion of microglial population in diseased conditions seems to improve tissue repair and promote functional improvement after spinal cord injury. Furthermore, we discuss the advantages and disadvantages of major strategies and timing of microglia depletion to provide potential strategy for the treatment of spinal cord injury.

Introduction: Failed back surgery syndrome is a situation where there is failure after lumbar surgery aimed at correcting lumbar disease that is characterized by continuous back and/or leg pain. Epidural fibrosis and adhesions are among the major causes of failed back surgery syndrome. In recent years, several biomaterials have been applied as barriers or deterrents to prevent the compression of neural structures by postsurgical fibrosis. Methods: In this study, a new bacterial cellulose (BC) anti-adhesion membrane, composed of exosomes from human umbilical cord mesenchymal stem cells, was developed. Its structure and morphology, water content, thickness, and mechanical properties of elasticity were analyzed and characterized. The degradation of the BC+exosomes (BC+Exos) membrane in vitro was evaluated, and its in vitro cytotoxicity and in vivo biocompatibility were tested. The prevention effect of BC+Exos membrane on epidural fibrosis post-laminectomy in a rabbit model was investigated. Results: The BC+Exos membrane showed a three-dimensional network structure constituted of high-purity cellulose and moderate mechanical properties. No degeneration was observed. The BC+Exos membrane showed no cytotoxicity and displayed biocompatibility in vivo. The BC+Exos film was able to inhibit epidural fibrosis and peridural adhesions. Conclusion: Based on the current findings, the BC+Exos membrane is a promising material to prevent postoperative epidural fibrosis and adhesion.

JOURNAL/nrgr/04.03/01300535-202507000-00029/figure1/v/2026-04-26T112544Z/r/image-tiff Autografting is the gold standard for surgical repair of nerve defects > 5 mm in length; however, autografting is associated with potential complications at the nerve donor site. As an alternative, nerve guidance conduits may be used. The ideal conduit should be flexible, resistant to kinks and lumen collapse, and provide physical cues to guide nerve regeneration. We designed a novel flexible conduit using electrospinning technology to create fibers on the innermost surface of the nerve guidance conduit and employed melt spinning to align them. Subsequently, we prepared disordered electrospun fibers outside the aligned fibers and helical melt-spun fibers on the outer wall of the electrospun fiber lumen. The presence of aligned fibers on the inner surface can promote the extension of nerve cells along the fibers. The helical melt-spun fibers on the outer surface can enhance resistance to kinking and compression and provide stability. Our novel conduit promoted nerve regeneration and functional recovery in a rat sciatic nerve defect model, suggesting that it has potential for clinical use in human nerve injuries.